Gelation Forming Process for Toxicity-Free or Low-Toxicity System

Yong Huang,Jinlong Yang

DOI: https://doi.org/10.1007/978-981-15-1872-0_3

2020-01-01

Abstract:In this chapter, the forming process of ceramics by gelling of agarose, gelatine and sodium algaecide has been presented, and another gel-casting system with low toxicity by using HEMA is also described. This study shows that gelled green bodies by the addition of agarose of 0.7 - 1.05 wt% and a solid loading of 53 - 55 vol% had a homogeneous density distribution and a green strength >3 MPa. Some simple and complex parts, such as a turbine rotor, were formed by this method. Gelatine can be dissolved in water above 40 degrees C, and the solutions gel at 15 - 20 degrees C. Wet green compacts can be formed from the alumina slurry containing 4 - 5 wt% gelatine (based on water) by gelation. A novel casting method by gelatine and enzyme catalysis is also described. As urease is added into the suspension, the gelatine molecules attract each other and change to a three-dimensional (3D) network structure through hydrogen bonding due to urea decomposition by urease. Then the slurry containing ceramic powder and gelatine will be consolidated in-situ by the gelation under ambient conditions. For the another gel-casting process by alginate, in which solidified agent and chelator are added into sodium alginate solution simultaneously; thus, the gelation between calcium ions and sodium alginate is avoided in this stage before casting. Free calcium ions are released when hexanedioic acid is added into the suspension. They react with sodium alginate and form a 3D network. Therefore, ceramic particles are fixed in this 3D network. The slurry is consolidated and near-net-shape green parts are formed. In addition, a new low toxic gel-casting system has been successfully developed by using HEMA or HEMA-PVP, by which dense and homogeneous complex-shaped alumina and silicon carbide parts have been successfully fabricated.