Dynamic recrystallization, twinning behaviors and mechanical response of pre-twinned AZ31 Mg alloy sheet along various strain paths at warm temperature
Xiaohuan Pan,Lifei Wang,Liangliang Xue,Sabbaghian,Pengbin Lu,Wei Wu,Guangsheng Huang,Bin Xing,Hongxia Wang,Mahdi Sabbaghian
DOI: https://doi.org/10.1016/j.jmrt.2022.05.164
IF: 6.267
2022-06-02
Journal of Materials Research and Technology
Abstract:In this study, AZ31 Mg alloy sheet was pre-twinned at room temperature along the transverse direction (TD) to introduce {10-12} tensile twins. The uniaxial tensile experiment was conducted at 200 °C to investigate the dynamic recrystallization, twinning behaviors and mechanical response. The strain paths tilted angles of 0°, 15°, 30°, 45°, 60°, 75° and 90° in respect to the rolling direction (RD) on the RD-TD plane were considered. Results revealed that the strain path has significant effects on the microstructural evolution and mechanical response at warm temperature. When the strain path tilts were 0°, 15°, 30°, 45° and 60° with the RD, continuous dynamic recrystallization (CDRX) was the main mechanism to coordinate strain. The detwinning dominated the microstructural evolution but retarded by CDRX for the pre-twinned sample with a strain path angle of 75°. Detwinning and CDRX played an important role on the microstructural evolution in the pre-twinned sample when the strain path was tilted 90°. Additionally, the effect of CDRX on {10-12} twinning and three types of {10-12} tensile twin behaviors were discussed. Both strengthening and weakening effects were observed in pre-twinned samples.
materials science, multidisciplinary,metallurgy & metallurgical engineering