Abstract:To enrich the properties of polylactic acid (PLA)-based composite films and improve the base degradability, in this study, a certain amount of poly(propylene carbonate) (PPC) was added to PLA-based composite films, and PLA/PPC-based composite films were prepared by melt blending and hot-press molding. The effects of the introduction of PPC on the composite films were analyzed through in-depth studies on mechanical properties, water vapor and oxygen transmission rates, thermal analysis, compost degradability, and bacterial inhibition properties of the composite films. When the introduction ratio coefficient of PPC was 30%, the tensile strength of the composite film increased by 19.68%, the water vapor transmission coefficient decreased by 14.43%, and the oxygen transmission coefficient decreased by 18.31% compared to that of the composite film without PPC, the cold crystallization temperature of the composite film increased gradually from 96.9 °C to 104.8 °C, and PPC improved the crystallization ability of composite film. The degradation rate of the composite film with PPC increased significantly compared to the previous one, and the degradation rate increased with the increase in the PPC content. The degradation rate was 49.85% and 46.22% faster on average than that of the composite film without PPC when the degradation was carried out over 40 and 80 days; the composite film had certain inhibition, and the maximum diameter of the inhibition circle was 2.42 cm. This study provides a strategy for the development of PLA-based biodegradable laminates, which can promote the application of PLA-based laminates in food packaging.

Preparation and Properties Study of Ultra-fine Talc Filled Poly(Lactic Acid) Films

Preparation and characterization of poly(L-lactide)-co-poly(trimethylene carbonate)/talc film

The Effect of Talc on the Mechanical, Crystallization and Foaming Properties of Poly(Lactic Acid)

Effects of talc on the mechanical and thermal properties of polylactide

Fabrication and characterization of poly(lactic acid-trimethylene carbonate) based biodegradable composite films

Crystallization improvement of PLA by the talc with "grafting from" method of polymerization of lactide

Study of Thermal, Mechanical and Barrier Properties of Biodegradable PLA/PBAT Films with Highly Oriented MMT

Characterization and Properties of Nucleated Polylactide, Poly(butylene adipate-co-terephthalate), and Thermoplastic Starch Ternary Blend Films: Effects of Compatibilizer and Starch

Ductile and biodegradable poly (lactic acid) matrix film with layered structure

Mechanical Characteristics and Barrier Properties of Polylactic Acid Films Prepared by Casting Method

Preparation and properties of PLA/PBAT composites modified with different filler particles

Effect of Dopamine Modified Talcum Powder on the Crystallization Behavior and Rheological Properties of PLA/PBS Blends

Thermoplastic starch/polyester films: effects of extrusion process and poly (lactic acid) addition

Effects of Inorganic Fillers on the Thermal and Mechanical Properties of Poly(lactic acid).

Influence of Biodegradable Poly(butylene Carbonate) on Plasticized Polylactide Blown Films

Effect of Mixing Poly(lactic Acid) with Glycidyl Methacrylate Grafted Poly(ethylene Octene) on Optical and Mechanical Properties of the Blown Films

Preparation and Characteristics of Poly(butylene adipate-co-terephthalate)/Polylactide Blend Films via Synergistic Efficiency of Plasticization and Compatibilization

Improved properties of poly(butylene adipate‐co‐terephthalate)/calcium carbonate films through silane modification

Facile method to improve toughness and biodegradability of polylactide by modified CaCO3

Effect of Poly(propylene carbonate) on Properties of Polylactic Acid-Based Composite Films

Enhancement of the properties of biodegradable poly(L-lactide)/poly(butylene carbonate) blends by introducing stereocomplex polylactide crystals