Effects of Poly(ε-caprolactone) on the Properties of Poly (lactic acid)/Poly (butylene succinate) Blends
Gu Ting,Zhu Dayong,Zheng Qiang,Yu Jie,Lu Shengjun
DOI: https://doi.org/10.16865/j.cnki.1000-7555.2018.02.008
2018-01-01
Abstract:Poly (lactic acid) /poly (butylene succinate) /poly (ε-caprolactone) (PLA/PBS/PCL) blends with different poly (ε-caprolactone) (PCL) contents (PCL content) were prepared by melt blending.And the crystallization property,thermal stability,rheological behavior and mechanical properties of PLA/PBS/PCL blends were studied by XRD,TG,rheometer and universal testing machine.The results show that the addition of PCL does not change the crystal structure of the blends;after addition of PCL,the initial decomposition temperature (Ti) and decomposition termination temperature (Tf) of the blends increase significantly,and when the PCL content is equal to 3 phr,Ti and Tf of the blends are increased by 27.14 ℃ and 23.31 ℃,respectively;and when the PCL content is less than or equal to 2 phr,PCL can improve the compatibility of blends,the comptibility between PLA and PBS is improved;and with the increase of PCL content,the tensile strength of the blends increases firstly and then decreases,when the PCL content is equal to 2 phr,it reaches the maximum value of 69.3 MPa,the impact strength of the blends is increased and when the PCL content is equal to 3 phr,it reaches the maximum value of 5.59 kJ/m2,they are increased by 35.4％ and 76.9％ compared with PLA/PBS blends,respectively.