Abstract:Uniform alpha-Fe(2)O(3) nanorods with diameter of about 30 nm and length up to 500 nm were synthesized by a template-free hydrothermal method and a following calcination of the intermediate product in the air at 500 degrees C for 2 h. By carefully tuning the concentration of the reactants, a series of alpha-Fe(2)O(3) nanorods with gradient in aspect ratios can be obtained. The effect of the solvent was also evaluated. Based on the experimental facts, the formation mechanism of this one-dimensional structure was proposed. The size-dependent properties of the as-obtained alpha-Fe(2)O(3) nanorods were investigated. The optical absorption properties of the samples showed that the band gaps of the samples decreased in the sequence in which the size increased. The electrochemical performance of the samples showed that the discharge capacity decreased as the size of the sample increased, which may result from the high surface area and small size. The magnetic hysteresis measurements taken at 5 K showed that the coercivities of the samples were related to the aspect ratios of the samples, which may result from the larger shape anisotropy. However, the temperature-dependent field cooling magnetization showed that there was no Morin transition in the as-prepared samples, which may result from the surface effect.

Synthesis of Β-Feooh and Α-Fe2o3nanorods and Electrochemical Properties of Β-Feooh

Synthesis and electrochemical properties of hierarchically porous Fe 2 O 3

Controlled morphology synthesis of β-FeOOH and the phase transition to Fe2O3

Synthesis And Lithium Storage Performance Of Alpha-Fe2o3-Ag Hybrid Nanorod Anode For Lithium-Ion Batteries

Electrochemical performance of α-Fe2O3 nanorods as anode material for lithium-ion cells

Synthesis and Characterization of Α-Feo(oh) Nano-Rods in Situ Via a Solution-Oxidation

Preparation and Catalytic Property of Single Crystal Multiporousα-Fe_2O_3 Nanorods

Hydrothermal Synthesis and Characterization of Uniform Α-Feooh Nanowires in High Yield

Synthesis Of Mesoporous Fe2o3 Nanorods And Their Electrochemical Performance

Synthesis of Fluorine-Doped Α-Fe2o3 Nanorods Toward Enhanced Lithium Storage Capability

Fabrication and Electrochemical Properties of Α-Fe2o3 Nanoparticles

Controlled Synthesis of Α-Fe2o3 Nanorods and Its Size-Dependent Optical Absorption, Electrochemical, and Magnetic Properties

Synthesis of Magnetite Nanorods Through Reduction of Β-Feooh

Morphology-controlled preparation of a-Fe 2 O 3 during evaporating aqueous FeCl 3 solution and investigating the electrochemical properties of various a-Fe 2 O 3 morphologies

Synthesis and Characterization of Fe-doped Vanadium Oxide Nanorods and Their Electrochemical Performance

Controlled synthesis of α-FeOOH nanorods and their transformation to mesoporous α-Fe2O3, Fe3O4@C nanorods as anodes for lithium ion batteries

A General Approach for MFe2O4 (M = Zn, Co, Ni) Nanorods and Their High Performance As Anode Materials for Lithium Ion Batteries

Facile Synthesis Of Single-Crystalline Mesoporous Alpha-Fe2o3 And Fe3o4 Nanorods As Anode Materials For Lithium-Ion Batteries

Synthesis and Electrochemical Performance of LiFePO4 Nanorods

Morphology-controlled Synthesis of Α-Feooh and Its Derivatives

FACILE SYNTHESIS OF alpha-Fe2O3 NANORODS DERIVED FROM alpha-FeOOH NANORODS AND ITS APPLICATION AS ANODE MATERIALS FOR RECHARGEABLE SODIUM-ION BATTERIES