Abstract:Uniform alpha-Fe(2)O(3) nanorods with diameter of about 30 nm and length up to 500 nm were synthesized by a template-free hydrothermal method and a following calcination of the intermediate product in the air at 500 degrees C for 2 h. By carefully tuning the concentration of the reactants, a series of alpha-Fe(2)O(3) nanorods with gradient in aspect ratios can be obtained. The effect of the solvent was also evaluated. Based on the experimental facts, the formation mechanism of this one-dimensional structure was proposed. The size-dependent properties of the as-obtained alpha-Fe(2)O(3) nanorods were investigated. The optical absorption properties of the samples showed that the band gaps of the samples decreased in the sequence in which the size increased. The electrochemical performance of the samples showed that the discharge capacity decreased as the size of the sample increased, which may result from the high surface area and small size. The magnetic hysteresis measurements taken at 5 K showed that the coercivities of the samples were related to the aspect ratios of the samples, which may result from the larger shape anisotropy. However, the temperature-dependent field cooling magnetization showed that there was no Morin transition in the as-prepared samples, which may result from the surface effect.

Controlled morphology synthesis of β-FeOOH and the phase transition to Fe2O3

Synthesis of Β-Feooh and Α-Fe2o3nanorods and Electrochemical Properties of Β-Feooh

Morphology-controlled Synthesis of Α-Feooh and Its Derivatives

Controllable Synthesis and Morphology Evolution of Hierarchical LiFePO4 Cathode Materials for Li-ion Batteries

Hydrothermal Synthesis of Β-Feooh with Different Morphologies Using NaH2PO4 As Structural Modifier

Preparation and Catalytic Property of Single Crystal Multiporousα-Fe_2O_3 Nanorods

Morphological Control of α-FeOOH Nanostructures by Electrodeposition

Synthesis and Characterization of Α-Feo(oh) Nano-Rods in Situ Via a Solution-Oxidation

Hydrothermal Synthesis and Characterization of Uniform Α-Feooh Nanowires in High Yield

Morphology-controlled synthesis of α-Fe2O3 nanostructures with magnetic property and excellent electrocatalytic activity for H2O2

Controlled synthesis and growth mechanism of hematite nanorhombohedra, nanorods and nanocubes

Room Temperature Synthesis Of Rod-Like Fec2o4 Center Dot 2h(2)O And Its Transition To Maghemite, Magnetite And Hematite Nanorods Through Controlled Thermal Decomposition

Room Temperature Synthesis of Rod-Like FeC{sub 2}o{sub 4}{center_dot}2h{sub 2}O and Its Transition to Maghemite, Magnetite and Hematite Nanorods Through Controlled Thermal Decomposition

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

Synthesis And Lithium Storage Performance Of Alpha-Fe2o3-Ag Hybrid Nanorod Anode For Lithium-Ion Batteries

Hydrothermal synthesis and characterization of α-FeOOH and α-Fe2O3 uniform nanocrystallines

Controlled Synthesis of Α-Fe2o3 Nanorods and Its Size-Dependent Optical Absorption, Electrochemical, and Magnetic Properties

Morphological Control Of Alpha-Feooh Nanostructures By Electrodeposition

Polyoxometalate-assisted One-step Fabrication of Porous Nanorods of Β-Feooh and the Facile Transition to Hematite

Synthesis of Magnetite Nanorods Through Reduction of Β-Feooh

Controlled synthesis of α-FeOOH nanorods and their transformation to mesoporous α-Fe2O3, Fe3O4@C nanorods as anodes for lithium ion batteries