FACILE SYNTHESIS OF alpha-Fe2O3 NANORODS DERIVED FROM alpha-FeOOH NANORODS AND ITS APPLICATION AS ANODE MATERIALS FOR RECHARGEABLE SODIUM-ION BATTERIES

Shubo Wang,Wei Wang,Liwen Hu,Zongqian Hu,Shuqiang Jiao,Hongmin Zhu

DOI: https://doi.org/10.1007/978-3-319-48237-8_104

2014-01-01

Abstract:alpha-Fe2O3 nanorods have been successfully obtained by annealing alpha-FeOOH precursor nanorods synthesized by a facile hydrothermal method. The electrochemical performance of the asprepared alpha-Fe2O3 a nanorods as anode materials for sodium-ion batteries is tested using galvanostatic charge/discharge cycling. The result indicates that the pcsudocapacitor effect dominates the charge/discharge process. The alpha-Fe2O3 synthesized at different temperature indicates that alpha-Fe2O3 with a high crystallinity manifests relatively better cycling ?erformance with a capacity of 177 mAh g-1 after 20 cycles at current density of 200 mA g(-1). While the current density increases to 500 mA g-1, the corresponding discharge capacity can still remain as much as 132 mAt center dot g(-1) Meanwhile, XPS spectrum results of the active electrode material asprepared and after a discharge process disclose that the electrochemical reaction mechanism happens in the half-cell sodium ion battery is the reduction of Fe2O3 to Fe.