Synthesis and lithium-ion storage performances of LiFe 0.5 Co 0.5 PO 4 /C nanoplatelets and nanorods
Yanjun Zhong,Zhenguo Wu,Juntao Li,Wei Xiang,Xiaodong Guo,Benhe Zhong,Xin Long Wang
DOI: https://doi.org/10.1007/s11581-017-2366-5
IF: 2.961
2017-01-01
Ionics
Abstract:Carbon-coated olivine-structured LiFe 0.5 Co 0.5 PO 4 solid solution was synthesized by a facile rheological phase method and applied as cathode materials of lithium-ion batteries. The nanostructure’s properties, such as morphology, component, and crystal structure for the samples, characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Brunauer, Emmett, and Teller (BET) determination, X-ray photoelectron spectroscopy (XPS), and the electrochemical performances were evaluated using constant current charge/discharge tests and electrochemical impedance spectroscopy (EIS). The results indicate that nanoplatelet- and nanorod-structured LiFe 0.5 Co 0.5 PO 4 /C composites were separately obtained using stearic acid or polyethylene glycol 400 (PEG400) as carbon source, and the surfaces of particles for the two samples are ideally covered by full and uniform carbon layer, which is beneficial to improving the electrochemical behaviors. Electrochemical tests verify that the nanoplatelet LiFe 0.5 Co 0.5 PO 4 /C shows a better capacity capability, delivering a discharge specific capacity of 133.8, 112.1, 98.3, and 74.4 mAh g −1 at 0.1, 0.5, 1, and 5 C rate (1 C = 150 mA g −1 ); the corresponding cycle number is 5th, 11th, 15th, 20th, and 30th, respectively, whereas the nanorod one possesses more excellent cycling ability, with a discharge capacity of 83.3 mAh g −1 and capacity retention of 86.9% still maintained after cycling for 100 cycles at 0.5 C. Results from the present study demonstrate that the LiFe 0.5 Co 0.5 PO 4 solid solution nanomaterials with favorable carbon coating effect combine the characteristics and advantage of LiFePO 4 and LiCoPO 4 , thus displaying a tremendous potential as cathode of lithium-ion battery.