Abstract:After Mg and Ni nanoparticles were fabricated by hydrogen plasma metal reaction, Mg-rich MgxNi100−x(75 < x < 90) materials were synthesized from these metal nanoparticles to study the synergistic effects for hydrogen storage in these samples to show both good kinetics and high capacity. These MgxNi100−x materials may absorb hydrogen with a capacity of around 3.3–5.1 wt% in 1 min at 573 K. The Mg90Ni10 sample shows a hydrogen capacity of 6.1 wt%. The significant kinetic enhancement is thought to be due to the unique nanostructure from the special synthesis route, the catalytic effect of the Mg2Ni nano phase, and the synergistic effects between the Mg2Ni and Mg phases in the materials. An interesting phenomenon which has never been reported before was observed during pressure composition isotherm (PCT) measurements. One steep step in the absorption process and two obviously separated steps in the desorption process during PCT measurements of Mg80Ni20 and Mg90Ni10 samples were observed and a possible reason from the kinetic performance of the Mg2Ni and Mg phases in absorption and desorption processes was explained. These MgxNi100−x materials synthesized from Mg and Ni nanoparticles show high capacity and good kinetics, which makes these materials very promising candidates for thermal storage or energy storage and utilization for renewable power.

Preparation and Hydrogen Storage Properties of Mg-Ni Based Hydrogen Storage Alloy

Preparation and Properties of Mg-based Hydrogen Storage Alloys for Hybrid Electric Vehicle

FeNiCu-based Composite Catalyst for Hydrogen Storage in MgH2

An electrochemical investigation of mechanical alloying of MgNi-based hydrogen storage alloys

Hydrogen storage properties of Mg-23.3wt.%Ni eutectic alloy prepared via hydriding combustion synthesis followed by mechanical milling

Hydrogen Storage Properties of Mg-doped Ti 1.2 Fe Alloys Synthesized by Mechanical Alloying

Magnesium-nickel Hydrogen Storage Alloys Prepared by Hydriding Combustion Synthesis Followed by Mechanical Milling

Phase-structure and Hydrogen Storage Behaviors of Mg+10％ Ni2P Composite Prepared by Reactive Ball-Milling

Microstructure and Hydrogen Storage Characteristics of Nanocrystalline Mg+xwt% LaMg2Ni (x=0–30) Composites

Effect of in-situ formed Mg2Ni/Mg2NiH4 compounds on hydrogen storage performance of MgH2

Preparation of Mg-based hydrogen storage materials from metal nanoparticles

Hydrogen storage in Mg2Ni(Fe)H4 nano particles synthesized from coarse-grained Mg and nano sized Ni(Fe) precursor

Review on Hydrogen Storage Property and Preparation of Nanostructured Mg

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Preparation and hydrogen storage properties of Mg-20 wt.% Mg 2Ni0.8Cr0.2 composite with TiO2 nanoparticles

Preparation and Hydrogen Storage Properties of Mg-20 Wt.% Mg<sub>2</sub>Ni<sub>0.8</sub>Cr<sub>0.2</sub> Composite with TiO<sub>2</sub> Nanoparticles

High Active Hydrogen Storage Alloy Mg<sub>2</sub>NiH<sub>4</sub> and Mg<sub>2</sub>Ni Synthesized at Temperatures Lower than 733 K

Phase, Microstructure and Hydrogen Storage Properties of Mg–Ni Materials Synthesized from Metal Nanoparticles

Preparation and hydrogen storage properties of nanostructured Mg2Cu alloy

Hydrogen Storage Properties of Mg100−xNix (x = 5, 11.3, 20, 25) Composites Prepared by Hydriding Combustion Synthesis Followed by Mechanical Milling (HCS + MM)

High active hydrogen storage alloy Mg2NiH4 and Mg2Ni synthesized at temperatures lower than 733 K