Abstract:In this study, the microstructural changes in irradiated W-1 wt%Pr2O3, W-1 wt%La2O3, W-1 wt%TiC and W-1 wt%ZrC specimens by 1 MeV Fe+ ion irradiation to doses of 1 dpa at room temperature have been characterized by transmission electron microscopy (TEM) to understand the radiation damage. The specimens of 1 dpa were consecutively annealed at temperatures of 600 degrees C, 800 degrees C, 900 degrees C and 1100 degrees C for 1h, and the post-irradiation annealing effect on the microstructure was studied. Microstructural features such as dislocations, dislocation loops and dense dislocation networks were observed by the means of TEM. There was a significant change in the microstructure of the tungsten (W) after irradiation and post-irradiation annealing. W-1 wt%TiC likely consisted of fewer radiation-induced defects and hence exhibits higher resistance to radiation-induced microstructural changes than the others. The general trend is that the density of defect clusters decreases while the average size of the clusters increases with the annealing temperature. A complete removal of dislocation structures at 1100 degrees C occurred in all materials. The irradiation damage effect of Fe+ ions on the deuterium retention of as-synthesized W-based composites was investigated. Thermal desorption spectroscopy of W implanted with D-2 (-) ions was performed using the low-energy ion irradiation system of Kyoto University. Compared with the samples without Fe preirradiation, the deuterium retention of the four composites increased after Fe+ pre-irradiation. The retained amount of deuterium was also increased with the increase in the Fe+ irradiation dose. This is of vital importance to the scientific community working on these materials for extreme irradiating environments.

Transient Thermal Response of Pure and Oxide Dispersion Strengthened Tungsten Alloys

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Experimental and Numerical Simulations of ELM-like Transient Damage Behaviors to Different Grade Tungsten and Tungsten Alloys

Mechanical Properties and Thermal Shock Performance of W-Y2O3composite Prepared by High-Energy-rate Forging

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Thermal change of microstructure and mechanical properties of dispersion strengthened tungsten

Surface Cracking of Tungsten-Vanadium Alloys under Transient Heat Loads

Microstructural Effects of Y2O3 and TiC Additions in Tungsten

Transient thermal shock behavior of W–Zr/Sc2O3 composites prepared via spark plasma sintering

Surface Damage During Transient Thermal Load of 50% Thickness Reduced W-2% (vol.) Y2O3 Sheet with Different Recrystallization Volume Fraction

Investigation of W–B Behavior During Short Transient Events by Laser Irradiation

Effect of intense pulsed ion beams irradiation on the properties of IC-6 alloys

TEM Studies of 1 MeV Fe+ Ion-Irradiated W Alloys by Wet Chemical Method: High-Temperature Annealing and Deuterium Retention

Molecular Dynamics Study of Thermal Stress and Heat Propagation in Tungsten under Thermal Shock

Transient thermal shock and helium ion irradiation damage behaviors of ODS-W/CuCrZr joints

Thermal shock behavior of W–ZrC/Sc2O3 composites under two different transient events by electron and laser irradiation

Thermal stability of the HPT-processed tungsten at 1250 – 1350 °C

DBTT and tensile properties of as-sintered tungsten alloys reinforced by yttrium-zirconium oxide

Transient grating spectroscopy of thermal diffusivity degradation in deuterium implanted tungsten

Room temperature ductile W-Y2O3 alloy with high thermal shock resistance

Surface Damage and Microstructure Evolution of Yttria Particle-Reinforced Tungsten Plate During Transient Laser Thermal Shock