Preparation of Mg70Ni15Gd10Ag5 Bulk Amorphous Alloys and Their Crystallization Behaviors

Hao Peng, ,Tianyou Huang,Bin Tang,Li Shuangshou

2010-01-01

Rare Metal Materials and Engineering

Abstract:A novel bulk amorphous alloy Mg70Ni15Gd10Ag5 (at%)was prepared by copper-mold casting, and its critical size was no less than 5 mm, which is the largest value of preparation size for Mg-Ni based alloys at present. The crystallization behavior of the bulk amorphous alloy during continuous heating was studied by differential scanning calorimeter (DSC). Results show that the crystallization of the amorphous alloy is multiple. With increasing of the heating rate, all the characteristic temperatures including glass transition temperature T-g, onset crystallization temperature T-x, peak crystallization temperatures T-p (T-p1, T-p2, T-p3 and T-p4), melting-starting temperature T-m and liquidus temperature T-1 shift to higher temperatures. The crystallization has remarkable dynamic characteristics. The activation energies Eg, E-x and E-p, corresponding to characteristic temperatures T-g, T-x and T-p were obtained by Kissinger equation, as E-g=188.05 kJ/mol, E-x=144.79 kJ/mol, E-p1=138 kJ/mol, E-p2=142.40 kJ/mol, E-p3=119.10 kJ/mol and E-p4=72.86 kJ/mol.