Investigation on the Microstructure and Mechanical Behaviors of a Laser Formed Nb-Ti-Al Alloy
Zhiwu Shi,Jinlai Liu,Hua Wei,Hongyu Zhang,Xiaofeng Sun,Qi Zheng
DOI: https://doi.org/10.1016/j.matchar.2020.110193
IF: 4.537
2020-01-01
Materials Characterization
Abstract:Nb-Ti-Al alloys have attracted much attention as a potential candidate for high-temperature structural applications beyond the scope of Ni-based superalloys. Previously, Nb-Ti-Al alloys were prepared by arc-melting or hot-pressing. In this study, laser forming of the Nb-23Ti-15Al alloy is explored, and the microstructure and mechanical behaviors are systematically investigated. The results indicate that the nearly defectless Nb-Ti-Al alloy with fine dendrites could be obtained through laser forming. Three phases, β, δ and Ti(O,C), present in the alloy, and the β/δ matrix displays a columnar microstructure. Moreover, the Ti(O,C) phase, a solid-solution of TiO or TiC, appears in the alloy. Ti(O,C) is formed due to the introduction of the O and C from the elemental powder, which has a face-centered cubic (FCC) structure and a moderate lattice parameter between that of TiO and TiC. Two morphologies of Ti(O,C), large cobblestone-like particles and small dispersive particles, are observed in the alloy. Forbidden reflections of δ phase occur due to double diffraction and slight superlattice reflections of β phase arise. Furthermore, refined β/δ phases and dispersed small Ti(O,C) result in higher microhardness and fracture toughness. In brief, our results indicate that laser forming is a potential method for manufacturing Nb-Ti-Al alloys with prominent properties.