Abstract:The effect of surface modification on enhancing the magnetic heating behavior of magnetic nano fluids were investigated, for this purpose Fe 3 O 4 nanoparticles were synthesized using co-precipitation method and surface modification was done using citric acid, ascorbic acid, tetraethyl orthosilicate (TEOS), polyvinyl alcohol (PVA) and polyethylene glycol (PEG). Experimental heating tests using AC magnetic field were done in the frequency of 100 kHz and different magnetic field (H) intensities. Theoretically the specific absorption rate (SAR) in magnetic nano fluids is independent of nanoparticles concentration but the experimental results showed different behavior. The theoretical SAR value @ H = 12kA.m –1 for Nano fluids containing bare Fe 3 O 4 nanoparticles was 11.5 W/g but in experimental tests the obtained value was 9.72 W/g for nano fluid containing 20,000 ppm of dispersed nanoparticles. The experimental SAR calculation was repeated for sample containing 10,000 ppm of nanoparticles and the results showed increase in experimental SAR that is an evidence of nanoparticles agglomeration in higher concentrations. The surface modification has improved the dispersion ability of the nanoparticles. The Ratio of SAR , experimental, 20000ppm to SAR , experimental, 10000ppm was 0.85 for bare Fe 3 O 4 nanoparticles dispersion but in case of surface modified nanoparticles this ratio has increased up to 0.98 that shows lower agglomeration of nanoparticles as a result of surface modification, although on the other hand the surface modification agents were magnetically passive and so it is expected that in constant concentration the SAR for bare Fe 3 O 4 nanoparticles to be higher than this variable for surface modified nanoparticles. At lower concentrations the dispersions containing bare Fe 3 O 4 nanoparticles showed higher SAR values but at higher concentrations the surface modified Fe 3 O 4 nanoparticles showed better results although the active agent amount was lower at them. Finally, it should be noted that the nanoparticles that were surface modified using polymeric agents showed the highest decrease in experimental SAR amounts comparing theoretical results that was because of the large molecules of polymers comparing other implemented surface modification agents.

Preparation of Oil-Based Stabilized Dispersion of Fe3O4 Nanoparticles

Improved Dispersion Stability of Water-Based Tio2 Nanofluids Through Combined Effects of Nanoparticle Mixing and Dispersant Addition

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Influence of Different Preparation Methods on Crystallisation and Morphology of Fe2o3 Nanoparticles

Preparation and characterization of Fe3O4 nanoparticles via a hydrothermal process with propanediol as the solvent

Preparation and Surface Modification of Fe<sub>3</sub>O<sub>4 &Lt;/sub>nano-Magnetic Powders

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

Efficient Oil-Water Separation with Amphipathic Magnetic Nanoparticles of Fe3O4@TiO2

Preparation of stable colloidal dispersion of surface modified Fe3O4 nanoparticles for magnetic heating applications

In Situ Dispersion of Non-Aqueous Fe3O4 Nanocolloids by Microdroplet Coalescence and Their Use in the Preparation of Magnetic Composite Particles.

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Preparation, Surface Functionalization and Application of Fe3O4 Magnetic Nanoparticles

Preparation and Characterization of the Novel Magnetic Nano-Sized Ferrite(Fe_3O_4) Particles Modified by C_(16)H_(33)NaO_2

Polystyrene coating of Fe3O4 particles using dispersion polymerization

Synthesis of Fe3O4 Nanoparticles and Their Magnetic Properties

Preparation of Composite Nanoparticles of Fe-Zn Bioxide Using Surface Modification and Their Subsequent Characterization

Preparation method of kerosene-based magnetic fluid in which oleic-acid-coated nano Fe3O4 disperses

Ultrafast Preparation Of Monodisperse Fe3o4 Nanoparticles By Microwave-Assisted Thermal Decomposition

Preparation of Fe_3O_4 Nanopieces and Its Tribological Property in Liquid Paraffin

Stability and Photothermal Properties of Fe3O4-H2O Magnetic Nanofluids