Abstract:In this work, a series of new Ni 76-x Co x Nb 4 P 16 B 4 (x = 5, 10, 15, in at.%) bulk metallic glasses (BMGs) with the maximum diameter in the range of 1.2–1.6 mm were prepared by combining fluxing and J-quenching technology. The effects of Co content on glass forming ability (GFA), thermal stability, mechanical properties, serrated-flow behaviors and corrosion performance of the present Ni-based BMGs were systematically investigated. The ranges of T g and ΔTx are 664–668 K and 21–31 K, respectively. Uniaxial compressive tests revealed that the present Ni-based BMGs have the compressive plastic strain ( εp ), yield strength ( δ y ), and fracture strength ( δ f ) that range from 16% to 27%, 2.1–2.6 GPa, and 2.2–3.6 GPa, respectively. The unprecedented mechanical properties originate from more icosahedral-like clusters (ILCs) and crystal-like clusters (CLCs) in the present Ni-based BMGs. It is found that the serrated-flow behaviors of the present Ni-based BMGs transition self-organized critical state (SOCs) into chaotic state (Cs) as plasticity decreases. The stick-slip dynamics were used to calculate the average shear-band velocity (ASBV), which shows an increasing trend as the Co content rises from 5 at.% to 15 at.%. Electrochemical measurements in 3.5 wt.% NaCl solution showed that the Ni 71 Co 5 Nb 4 P 16 B 4 BMG has a self-corrosion current density of 3.30 × 10 −8 A/cm 2 and significantly stronger corrosion resistance than austenite 316L and 304L stainless steel. The present Ni-based BMGs have excellent comprehensive performance, which has great potential for industrial applications.

Mg–Ni–(Gd,Nd) Bulk Metallic Glasses with Improved Glass-Forming Ability and Mechanical Properties

Mg–Ni–Gd–Ag Bulk Metallic Glass with Improved Glass-Forming Ability and Mechanical Properties

Formation, Microstructure, and Mechanical Properties of in Situ Mg-Ni-(Gd,Nd) Bulk Metallic Glass Composite

A New Mg 65 Cu 7.5 Ni 7.5 Zn 5 Ag 5 Y 10 Bulk Metallic Glass with Strong Glass-Forming Ability

Mg–Cu–(Y,Nd) Pseudo-Ternary Bulk Metallic Glasses: the Effects of Nd on Glass-Forming Ability and Plasticity

Glass Forming Ability and Mechanical Properties of New Ni-Based Bulk Metallic Glasses

Ductile Ni-based bulk metallic glasses at room temperature

The Novel Ti-based Metallic Glass with Excellent Glass Forming Ability and an Elastic Constant Dependent Glass Forming Criterion

A new Mg65Cu7.5Ni7.5Zn5Ag 5Y10 bulk metallic glass with strong glass-forming ability

The Effect of Ni Substitution on the Glass-Forming Ability and Mechanical Properties of Mg–Cu–Gd Metallic Glass Alloys

Critical size and strength of the best bulk metallic glass former in the Mg–Cu–Gd ternary system

Progress in Research on Mg-Based Bulk Metallic Glasses

La-based bulk metallic glasses with critical diameter up to 30mm

Lightweight Ti–Zr–Be–Al Bulk Metallic Glasses with Improved Glass-Forming Ability and Compressive Plasticity

Mg-based Bulk Metallic Glass Composites with Plasticity and Gigapascal Strength

Zr–(Cu,Ag)–Al Bulk Metallic Glasses

Quaternary Ti–Zr–Be–Ni Bulk Metallic Glasses with Large Glass-Forming Ability

Centimeter-sized Ti-rich Bulk Metallic Glasses with Superior Specific Strength and Corrosion Resistance

Ductile Co-based Bulk Metallic Glass with Superhigh Strength and Excellent Soft Magnetic Properties Induced by Modulation of Structural Heterogeneity

A Ti–Zr–Be–Fe–Cu Bulk Metallic Glass with Superior Glass-Forming Ability and High Specific Strength

Ni-free Zr-based bulk metallic glasses with critical diameter above 20mm