Abstract:Twin roll casting has been used to produce sheet of Mg60Cu29Gd11 bulk metallic glass (BMG). Sheet can be produced with thicknesses between 1 and 4 mm, the width of sheet produced can be between 25 and 75 mm. The dimensional stability of the produced sheet in a cast run is ±1 mm in the width direction and ±0.05 mm in the thickness direction. As with all magnesium-based BMGs the sheet produced is strong yet brittle at room temperature. The maximum flexural stress of a twin roll cast Mg60Cu29Gd11 BMG strip is 150 MPa with a flexural strain of 0.005. The Charpy impact energy of a Mg60Cu29Gd11 BMG strip is 0.02 J. In order to improve the toughness values of the Mg60Cu29Gd11, BMG strip laminates of BMG and aluminum alloy (UNS A91100) were produced via roll bonding. The introduction of aluminum layers to the sheet structure provides a barrier to shear band movement stopping the sudden catastrophic failure of the sheet. After rolling the BMG was examined via X-ray diffraction (XRD) to confirm that the BMG layer remained amorphous. The flexural stress, flexural strain, and Charpy impact energy properties of BMG-Al laminates are improved when compared to monolithic glass properties. The flexural stress values for laminates compared to the monolithic glass improve by 60 pct from 150 to 250 MPa. The flexural strain values improve by over an order of magnitude from 0.005 to 0.14. The Charpy impact energies increase by 2 orders of magnitude from 0.02 to 2.5 J.

Mg–Ni–Gd–Ag Bulk Metallic Glass with Improved Glass-Forming Ability and Mechanical Properties

Mg–Ni–(Gd,Nd) Bulk Metallic Glasses with Improved Glass-Forming Ability and Mechanical Properties

A New Mg 65 Cu 7.5 Ni 7.5 Zn 5 Ag 5 Y 10 Bulk Metallic Glass with Strong Glass-Forming Ability

A new Mg65Cu7.5Ni7.5Zn5Ag 5Y10 bulk metallic glass with strong glass-forming ability

Formation, Microstructure, and Mechanical Properties of in Situ Mg-Ni-(Gd,Nd) Bulk Metallic Glass Composite

Preparation and Mechanical Properties of Mg-Ni-Gd-Ag Amorphous Alloy

La-based bulk metallic glasses with critical diameter up to 30mm

Critical size and strength of the best bulk metallic glass former in the Mg–Cu–Gd ternary system

The Effect of Ni Substitution on the Glass-Forming Ability and Mechanical Properties of Mg–Cu–Gd Metallic Glass Alloys

Glass Formability, Thermal Stability and Mechanical Properties of La-Based Bulk Metallic Glasses

Zr–(Cu,Ag)–Al Bulk Metallic Glasses

The Novel Ti-based Metallic Glass with Excellent Glass Forming Ability and an Elastic Constant Dependent Glass Forming Criterion

Mg-based Bulk Metallic Glass Composites with Plasticity and Gigapascal Strength

Improvement of corrosion resistance in NaOH solution and glass forming ability of as-cast Mg-based bulk metallic glasses by microalloying

A Centimeter-Sized Quaternary Ti-Zr-Be-Ag Bulk Metallic Glass

Production and Mechanical Properties of Roll Bonded Bulk Metallic Glass/Aluminum Laminates

Mg–Cu–(Y,Nd) Pseudo-Ternary Bulk Metallic Glasses: the Effects of Nd on Glass-Forming Ability and Plasticity

Effect of Ag substitution for Ti on glass-forming ability, thermal stability and mechanical properties of Zr-based bulk metallic glasses

Glass Forming Ability and Corrosion Resistance of Zr-Cu- Ni-Al-Ag Bulk Metallic Glass

Progress in Research on Mg-Based Bulk Metallic Glasses

Glass Forming Ability and Mechanical Properties of New Ni-Based Bulk Metallic Glasses