Abstract:To study the influence of creep recovery on the fracture properties of concrete, the pre-notched specimens were firstly subjected to three-point bending (TPB) loading at 60% peak load (Pmax) over 30 days. Afterwards, the load was removed and the creep recovery tests were performed for 1, 2, 3 and 15 days, respectively. Thereafter, the quasi-static TPB tests were conducted on the creep recovery specimens. The deformation versus time curves, initial cracking load (Pini), peak load and fracture energy in the quasi-static TPB tests after creep recovery were obtained. Also, the numerical analyses were conducted by combining with the Norton-Bailey model to investigate the stress variations at the crack tip and the time-dependent behaviour of concrete. By comparing the fracture parameters for the specimens with and without undergoing creep recovery, the effects of creep recovery on the fracture characteristics of concrete were assessed. The results showed that during the creep stage, the stress relaxation generated at the crack tip due to viscoelastic characteristics of concrete enlarged the deformation. In contrast, the reversed stress would occur at the crack tip during the recovery stage, and its relaxation over the time contributed to the time-dependent deformation during the creep recovery stage. By comparing with the specimens under the quasi-static TPB loading, Pini and Pmax for the creep recovery specimens would increase, and the increments slowed down over the recovery time. However, the increases in Pini and Pmax for the creep recovery specimens could not enhance the initial and critical fracture toughnesses and these toughnesses were approximately equal to those under the quasi-static tests.

Microstudy on Creep of Concrete at Early Age under Biaxial Compression

Biaxial Creep of High-Strength Concrete at Early Ages Assessed from Restrained Ring Test

Biaxial Creep Test Study on the Influence of Structural Anisotropy on Rheological Behavior of Hard Rock

Creep Characterization of Concrete Suffering Initial Damage

Early Age Properties and Cracking Control of Concrete

Fracture Toughness And Microstructure Of Concrete At Early-Ages

Tensile Creep of High Performance Concrete Under Restrained Condition

Study of the Behavior of Concrete under Triaxial Compression

A Microscopic Approach to Rate Effect on Compressive Strength of Concrete

Biaxial Behaviour Of Plain Concrete Subjected To Dynamic Compression With Constant Lateral Stress

Experimental study on fracture properties of self-compacting concrete

Microprestress solidification theory-based experimental and modeling of early-age concrete tensile creep at elevated temperatures

Dynamic Behaviour of Concrete in Biaxial Compression

Micro-mechanisms of Concrete Failure under Cyclic Compression: X-ray Tomographic In-Situ Observations

Strength and Deformation Characteristics of Concrete under Dynamic Biaxial Loading

Experimental Study of the Creep Effect on the Mechanical Properties of Concrete

Effects of creep recovery on the fracture properties of concrete

Tensile Creep Behavior of Concrete Subject to Constant Restraint at Very Early Ages

Decoupling of Autogenous Shrinkage and Tensile Creep Strain in High Strength Concrete at Early Ages

Comparison of Compressive, Tensile, and Flexural Creep of Early-Age Concretes under Sealed and Drying Conditions

Micro-cantilever testing on the short-term creep behaviour of cement paste at micro-scale