Self-assembling multi-layer Pd nanoparticles onto Nafion™ membrane to reduce methanol crossover
Haolin Tang,Mu Pan,Sanping Jiang,Zhaohui Wan,Runzhang Yuan
DOI: https://doi.org/10.1016/j.colsurfa.2005.04.011
2005-01-01
Abstract:Methanol crossover through the proton exchange membranes (PEMs, e.g., Nafion™ membrane) is one of the major obstacles that currently prevent the widespread commercial applications of direct methanol fuel cell (DMFC). In this paper, multi-layer self-assembly Nafion™ membranes (MLSA Nafion™ membranes) were prepared by alternately assembling charged Pd particles and Nafion ionmers onto Nafion™ membranes. The Pd particles, size of about 1.8nm in average, are charged by PDDA ionomers with zeta potential of 30mV (pH value of 8.5). The Pd loading of the first-layer MLSA Nafion™ membranes was 0.63μgcm−2, and the surface coverage of the Pd nanoparticles on the Nafion™ membrane was estimated as 22%. After 5-double-layer Pd particles/Nafion ionomers assembling, the Pd loading reached to 2.86μgcm−2. The methanol crossover current of the original Nafion™ membranes and 1-double-layer, 2-double-layer, 3-double-layer, 4-double-layer, 5-double-layer MLSA Nafion™ membranes were 0.0495, 3.87E−3, 1.38E−3, 7.32E−4, 5.16E−4 and 4.25E−4Acm−2, respectively, corresponding conductivities of 0.112, 0.110, 0.105, 0.094, 0.087 and 0.081Scm−2. This satisfactory performance has given the MLSA Nafion™ membranes a promised prospect of using as proton exchange membrane in direct methanol fuel cells.