Abstract:Perfluoroalkyoxy-substituted cyclohexene oxides(EFPO1 and EFPO2) were obtained by two-step reactions using the dimer and trimer of hexafluoropropylene oxide and 4-cyclohexene-1,2-dimethanol as main raw materials.The structures of as-synthesized products were confirmed by spectroscopy analyses including FT-IR and 1H NMR.These fluoro-epoxides are compatible with the prepolymers such as bisphenol-A diglycidyl ether and ethylene glycol diglycidyl ether,thereby endowing the coatings composed of them with improved hydrophobicity as evidenced by the photoinitiated curing experiments.The preliminary investigation of their UV-curing performance shows that the hydrophobicity increases linearly with increasing fluoro-epoxide content in the composition.As expected,the hydrophobic effect is more pronounced for EFPO2 than EFPO1 at the same conditions,because the former has a longer ferfluoroalkyoxy group.For example,upon addiing 1% mass fraction of EFPO2,the water contact angle of the UV-cured films was 99° and was higher 14° than that found for the films without the fluoro-component,whereas the value for EFPO1-modified films was 87°.When containing 5% EFPO2,high hydrophobic surface was achieved with a water contact angle of 113 for the UV-cured films.In addition,it should be pointed out that the hydrophobic surface can be further improved by heating the UV-cured films at 110 ℃ for 6 h.For the coatings containing 1%~5% EFPO2,the post-heating treatment resulted in a change of the water contact angles from the range 99°~113° to 113°~118°,while the changes were from 87°~100° to 99°~110° for EFPO1 analogs.The thermal migration of fluoro-chains and aggregation on the film surface seems to be responsible for the enhancement in hydrophobicity.Consequently,this new type of fluorine-containing epoxy monomers is expected as the surface modifier used in coatings,inks and release materials.

Fluorination of Epoxy Surfaces by a Physical Method

Synthesis and properties of an epoxy resin containing trifluoromethyl side chains and its cross-linking networks with different curing agents

Improving Insulation Properties of Epoxy Filled with Surface Fluorinated Polystyrene Nanospheres

Synthesis and characterization of fluorine-containing polyester based on phthalic anhydride and tetrafluoropropyl glycidyl ether

Synthesis Of Fluoroalkyl-Modified Polyester And Its Application In Improving The Hydrophobicity And Oleophobicity Of Cured Polyester Coatings

Improving the Hydrophilicity of Poly(vinylidene Fluoride) Porous Membranes by Electron Beam Initiated Surface Grafting of AA/SSS Binary Monomers

Preparation and fluorine enrichment behavior of fluorinated polyester

Influence of surface fluorination on surface wetting property of epoxy resin and its mechanism

Synthesis of New Fluorinated Epoxides and Preliminary Investigations on Their UV-curing Properties

Synthesis of Fluorinated Polyester Used for Hydrophobic Coating: Influence of Fluoroalkyl Group Length on Enrichment Behavior

Enhancement of surface electrical performances of epoxy film by blending with fluorinated and crosslinking monomer

A Simple Photochemical Method for Surface Fluorination Using Perfluoroketones

Enhanced Wettability and Adhesive Property of PTFE through Surface Modification with Fluorinated Compounds

Fluorine Gas Treatment Improves Surface Degradation Inhibiting Property of Alumina-Filled Epoxy Composite

Effect of fluorine hybridization on dielectric response of epoxy polymer

Post-Polymerization Modification of Fluoropolymers Via UV Irradiation in the Presence of a Photoacid Generator.

Modification of fluoropolymers by means of electron beam irradiation

Surprising Hydrophobic Polymer Surface with a High Content of Hydrophilic Polar Groups

Synthesis of Fluoro-(Meth) Acrylates and Performance of the UV-Curing Films

Preparation and properties of one epoxy system bearing fluorene moieties

Preparation, Characterization, and Properties of Fluorinated Polyurethanes