Abstract:Perfluoroalkyoxy-substituted cyclohexene oxides(EFPO1 and EFPO2) were obtained by two-step reactions using the dimer and trimer of hexafluoropropylene oxide and 4-cyclohexene-1,2-dimethanol as main raw materials.The structures of as-synthesized products were confirmed by spectroscopy analyses including FT-IR and 1H NMR.These fluoro-epoxides are compatible with the prepolymers such as bisphenol-A diglycidyl ether and ethylene glycol diglycidyl ether,thereby endowing the coatings composed of them with improved hydrophobicity as evidenced by the photoinitiated curing experiments.The preliminary investigation of their UV-curing performance shows that the hydrophobicity increases linearly with increasing fluoro-epoxide content in the composition.As expected,the hydrophobic effect is more pronounced for EFPO2 than EFPO1 at the same conditions,because the former has a longer ferfluoroalkyoxy group.For example,upon addiing 1% mass fraction of EFPO2,the water contact angle of the UV-cured films was 99° and was higher 14° than that found for the films without the fluoro-component,whereas the value for EFPO1-modified films was 87°.When containing 5% EFPO2,high hydrophobic surface was achieved with a water contact angle of 113 for the UV-cured films.In addition,it should be pointed out that the hydrophobic surface can be further improved by heating the UV-cured films at 110 ℃ for 6 h.For the coatings containing 1%~5% EFPO2,the post-heating treatment resulted in a change of the water contact angles from the range 99°~113° to 113°~118°,while the changes were from 87°~100° to 99°~110° for EFPO1 analogs.The thermal migration of fluoro-chains and aggregation on the film surface seems to be responsible for the enhancement in hydrophobicity.Consequently,this new type of fluorine-containing epoxy monomers is expected as the surface modifier used in coatings,inks and release materials.

Synthesis of Fluoro-(Meth) Acrylates and Performance of the UV-Curing Films

Synthesis of New Fluorinated Epoxides and Preliminary Investigations on Their UV-curing Properties

Hydrophobicity of Polyacrylate Emulsion Film Enhanced by Introduction of Nano-SiO₂ and Fluorine

Synthesis and characterization of fluorine-containing polyester based on phthalic anhydride and tetrafluoropropyl glycidyl ether

Synthesis Of Fluoroalkyl-Modified Polyester And Its Application In Improving The Hydrophobicity And Oleophobicity Of Cured Polyester Coatings

Preparation and characterization of fluorine-containing acrylate copolymers by 60Co γ-ray radiation co-polymerization

Properties and Characterization of Novel Cationic Polyacrylate Latex Containing Fluorine and Silicon Prepared with Soap-Free Emulsion Polymerization

Synthesis and Properties of Fluoropolyacrylate Coatings

Influence of Fluorine-Containing Monomer Content on the Hydrophobic and Transparent Properties of Nanohybrid Silica Polyacrylate Coating Materials

The Effect of Oxetane as Active Diluent on Cationic UV Curing System of Fluorine-Containing Epoxy Prepolymer

UV-curable waterborne epoxy acrylate coating modified by monomethacryloyloxy-terminated fluorinated oligomer

Synthesis and Performance of Novel Fluorinated Acrylate Polymers: Preparation and Reactivity of Short Perfluoroalkyl Group Containing Monomers

Preparation of fluorinated polysiloxane and its application in modified polyacrylates

Synthesis and characterization of fluorinated polyacrylate latex emulsified with novel surfactants

Synthesis and Characterization of Hyperbranched and Organosilicone Modified Waterborne Polyurethane Acrylates Photosensitive Resin

Fabricating superhydrophobic surfaces via coating amine-containing fluorinated emulsion and Michael addition reaction

Hydrophobicity of Polyacrylate Emulsion Film Enhanced by Introduction of Nano-SiO<sub>2</sub> and Fluorine

Hydrophobicity of Polyacrylate Emulsion Film Enhanced by Introduction of Nano-SiO2 and Fluorine

Synthesis and UV-curing of Waterborne Acrylated Polyurethanes

Preparation of UV-Curable Low Surface Energy Polyurethane Acrylate/Fluorinated Siloxane Resin Hybrid Coating with Enhanced Surface and Abrasion Resistance Properties