Preparation and Film Properties of Cross-Linking Siliconated Polyurethane-Fluorinated Acrylate Hybrid Emulsion
Xin-yan Xiao,Xi-song Cai,Cai-xia Wan
DOI: https://doi.org/10.3969/j.issn.1000-565X.2013.10.003
2013-01-01
Abstract:Siliconated polyurethane (SiPU) emulsion containing the unsaturated double bond was prepared via the solution polymerization, with isophorone diisocyanate (IPDI), polypropylene glycol (PPG), hydroxypropyl terminated polydimethyl sioxane (PDMS), trimethylolpropane (TMP), hydroxypropyl methacrylate (HPMA) and dimethylol propionic acid (DMPA) as main materials. Then, the cross-linking siliconated polyurethane-fluorinated acrylate hybrid emulsion (FSiPUA) was prepared via the radical emulsion polymerization, with SiPU as the seed emulsion and with butyl acrylate (BA), methyl methacrylate (MMA) and dodecafluoroheptyl methacrylate (DFMA) as the main monomers. Finally, the influences of HPMA, PDMS and DFMA dosages on the emulsion polymerization process and the film properties were discussed, and the PUA emulsion, the SiPUA emulsion and the FSiPUA hybrid emulsion as well as their films were characterized by using a Malvern particle size analyzer and a contact angle meter and by means of FT-IR, TG-DSC, XPS and AFM. The results indicate that, when the HPMA, PDMS and DFMA dosages are respectively 5.2%, 7.0% and 20.0%, the FSiPUA hybrid emulsion possesses good water resistance and high hydrophobicity, and that, owing to the addition of HPMA, PDMS and DFMA, the thermal stability and mechanical properties of the latex film are greatly improved with a higher surface roughness, a bigger water contact angle, a higher hydrophobicity and a lower water absorption.