Abstract:Process of irradiation modification of polytetrafluoroethylene above melting point. The cross‐linked polytetrafluoroethylene (PTFE) and PTFE/carbon fiber (CF) composites were synthesized through electron beam irradiation in the molten state of PTFE at a controlled temperature of 340 ± 3°C under an inert gas atmosphere for this study. The wear resistance of raw (raw‐PTFE), irradiated modified PTFE (RM‐PTFE), and CF‐reinforced PTFE composites were evaluated using a friction and wear testing machine. The testing was conducted under varying ambient temperatures and dynamic loads. After irradiation, the samples were sectioned into specific sizes for subsequent testing purposes. Under the test conditions of 4.64 MPa positive pressure, 800 rpm speed, and a duration of 300 s at 20°C, the wear amount of PTFE after irradiation modification is significantly reduced from 1.4103 mm to only 0.0233 mm, representing a remarkable reduction by a factor of 60. Similarly, under the test conditions of 4.64 MPa positive pressure, 200 rpm speed, and a duration of 300 s at 20°C, the friction coefficient of PTFE after irradiation modification is substantially decreased from an initial value of 0.13 to just 0.03. The observed improvement can be attributed to the transformation of PTFE's crystalline form into spherulite, accompanied by a significant enhancement in the degree of cross‐linking within its molecular chain. The PTFE was supplemented with 10% CF prior to irradiation. Under the test conditions of a positive pressure of 4.64 MPa, rotation speed of 800 rpm, and a duration time of 300 s at 20°C, the wear amount of the composite material measured only 0.0007 mm, representing a reduction by a factor of 2000 compared to that observed for pure PTFE. This improvement can be attributed to the CF filler's high wear resistance properties and the composite's enhanced thermal conductivity.

Modification of fluoropolymers by means of electron beam irradiation

Improving the Hydrophilicity of Poly(vinylidene Fluoride) Porous Membranes by Electron Beam Initiated Surface Grafting of AA/SSS Binary Monomers

Electron irradiation enhanced wear resistance and hardness of polytetrafluoroethylene (PTFE)

The radiation degradation of polytetrafluoroethylene resulting in low-molecular and functionalized perfluorinated compounds

Effect of irradiation modification above melting point on the wear resistance of polytetrafluoroethylene

Surface modification of PVDF porous membranes by electron irradiation

Controlled Grafting of Comb Copolymer Brushes on Poly(tetrafluoroethylene) Films by Surface-Initiated Living Radical Polymerizations.

Synthesis and characterization of fluorine-containing polyester based on phthalic anhydride and tetrafluoropropyl glycidyl ether

Tribological and Mechanical Behavior of Graphite Composites of Polytetrafluoroethylene (PTFE) Irradiated by the Electron Beam

Super antiwear properties of polytetrafluoroethylene (PTFE) induced by MeV proton irradiation

Enhanced Wettability and Adhesive Property of PTFE through Surface Modification with Fluorinated Compounds

Surface Modification of Poly(tetrafluoroethylene) Films Via Plasma Treatment and Graft Copolymerization of Acrylic Acid

Preparation and fluorine enrichment behavior of fluorinated polyester

Advances on Hydrophilic Modification of Polytetrafluoroethylene Porous Membrane

Femtosecond laser texturing assisted cold plasma hydrophilization of polytetrafluoroethylene surface

Polymer surface reactivity enhancement by ultraviolet ArF laser irradiation: An x‐ray photoelectron spectroscopy study of polytetrafluoroethylene and polyethyleneterepthalate ultraviolet treated surfaces

Surface Grafting Polymerization and Modification on Poly (tetrafluoroethylene) Films by Means of Ozone Treatment

Deposition of PTFE thin films by ion beam sputtering and a study of the ion bombardment effect

Surface-restructuring behavior of aged PTFE irradiated by a high-flux nitrogen ion beam

Synthesis Of Fluoroalkyl-Modified Polyester And Its Application In Improving The Hydrophobicity And Oleophobicity Of Cured Polyester Coatings

Surface modification of polytetrafluoroethylene (PTFE) fibers through methyl methacrylate (MMA) polymerization for self-lubricating composites