Abstract:Spinel LiMgxMn2-xO4 cathode materials were synthesised using a hydrothermal method, with the effects of doping Mg on the structure and electrochemical performance of LiMn2O4 subsequently investigated. It was found that no other hybrid phases existed in the LiMgxMn2-xO4 and that doped Mg cannot change the spinel lattice type of LiMn2O4. An appropriate Mg content was beneficial for improving the crystallinity and particle uniformity of the samples. The electrochemical performance of the LiMgxMn2−xO4 was assessed in the 2.9~4.3 V range, with the specific discharge capacity of the LiMn2O4 potentially reaching 139.9 mAh g−1 at 0.2 C, with a capacity retention rate of 63.76% after 100 cycles. Furthermore, the LiMn1.97Mg0.03O4 demonstrated an excellent cycling performance at both room temperature (25°C) and at a high temperature (55°C). At 25°C, the first specific discharge capacity was 124.3 mAh g−1 at 0.2 C, with a capacity retention rate of 94.29% after 100 cycles, while the specific discharge capacity can reach 94.8 mAh g−1 at 5 C and 74.0 mAh g−1 at 10 C. At 55°C, the initial specific discharge capacity was 125.6 mAh g−1 at 0.2 C, with a capacity retention rate of 85.43% after 100 cycles. The cyclic voltammogram curves and electrochemical impedance spectroscopy results indicated that, compared with the pristine LiMn2O4, the LiMn1.97Mg0.03O4 had a larger Li+-ion diffusion coefficient and smaller resistance during the charge–discharge process. Overall, the results indicated that Mg doping is beneficial in improving the electrochemical performance of spinel LiMn2O4.

Synthesis of spinel LiMn2O4 nanoparticles through one-step hydrothermal reaction

Hydrothermal Synthesis and Electrochemical Behavior of Nanosized Orthorhombic Limno2

One-Step Synthesis Limn2o4 Cathode by A Hydrothermal Method

Direct Hydrothermal Synthesis of LiMn 2 O 4 Spinel and Lithium Ion Selective Adsorption

Hydrothermal Synthesis of Layer LiMnO2

Direct hydrothermal synthesis of ternary Li-Mn-O oxide ion-sieves

Hydrothermal Synthesis and Lithium Adsorption Properties of LiMn_2O_4 Spinel

LIMN2O4 SPINEL DIRECT SYNTHESIS AND LITHIUM ION SELECTIVE ADSORPTION

Hydrothermal Synthesis of Flower-Like LiMnPO4nanostructures Self-Assembled with (010) Nanosheets and Their Application in Li-ion Batteries

Preparation of Submicrocrystal LiMn2O4 Used Mn3O4 As Precursor and Its Electrochemical Performance for Lithium Ion Battery

Synthesis and Electrochemical Performance of LiMnPO4by Hydrothermal Method

Hydrothermal Synthesis of Monodispersed LiMnPO4 (010) Nanobelts and [001] Nanorods and Their Applications in Lithium-Ion Batteries: Hydrothermal Synthesis of Monodispersed LiMnPO4 (010) Nanobelts and [001] Nanorods and Their Applications in Lithium-Ion Batteries

From Hydrated Layered-Spinel Lithium Manganate Composite to High-Performance Spinel Limn2o4: A Novel Synthesis Tuned by the Concentration of Lioh

Hydrothermal Synthesis of Monodispersed LiMnPO4 (010) Nanobelts and [001] Nanorods and Their Applications in Lithium-Ion Batteries

Microemulsion‐Assisted Synthesis of Nanosized LiMnO Spinel Cathodes for High‐Rate Lithium‐Ion Batteries

Electrochemical Performance of Nanosized LiMn2O4 for Lithium-Ion Batteries

Hydrothermal synthesis of Mg-doped LiMn2O4 spinel cathode materials with high cycling performance for lithium-ion batteries

Hydrothermal synthesis of orthorhombic LiMnO<sub>2</sub> nano-particles and LiMnO<sub>2</sub> nanorods and comparison of their electrochemical performances

Hydrothermal Synthesis and Electrochemical Performance of LiNi<sub>0.5</sub>Mn<sub>0.5</sub>O<sub>2</sub> as Lithium-Ion Battery Cathode

Hydrothermal synthesis of orthorhombic LiMnO 2 nano-particles and LiMnO 2 nanorods and comparison of their electrochemical performances

Synthesis of Highly Crystalline Spinel Limn2o4 by A Soft Chemical Route and Its Electrochemical Performance