Enhanced Low-Field Magnetoresistence in the Absence of Mn Content in Polycrystalline La 0.67 Ca 0.33 MnO 3

Zhao Lifeng,Chen Wei,Miao Juhong,Shang Jinglin,Yu Gongqi,Xiao Xun,Xia Zhengcai,Yuan Songliu

DOI: https://doi.org/10.1007/s11595-006-3510-7

2007-01-01

Abstract:Magnetic and electrical transport properties of the La 0.67 Ca 0.33 Mn 1− x O 3 ( x =0-0.16), which were prepared by the sol-gel method followed by sintering treatment at 1 450, 1 100 and 900°C, respectively, were investigated. Experimental results show that, with the increase of x , the resistivity of samples increases and the insulator-metal transition temperature shifts towards lower temperature. Meanwhile, the intrinsic megnetoresistance effect is weakened and the extrinsic magnetoresistance is enhanced. For the samples with x =0.16 and 0.10 sintered at 1 100 °C and 900 °C, respectively, low field magnetoresistance as high as about 50% can be observed. Furthermore, for the samples sintered at 1 100 °C and 900 °C, the grain size is not only controlled by about sintering temperature, but also by the absence of Mn content x .