Abstract:Understanding the initiating and suppression mechanisms of existing defects are the key to optimizing the ultra-precision grinding process of hard and brittle materials. This paper discusses the effects of grinding damage on material removal mechanism from the perspectives of residual scratch depth, scratch morphology and normal scratching force, through conducting the contrast variable-depth nano-scratch experiment on polished and ground monocrystalline silicon and establishing the single grain scratching Smoothed Particle Hydrodynamics (SPH) model. The experimental and simulation results show that radial crack on ground silicon surface is almost invisible due to the existence of grinding marks, which indicates that it is difficult to judge the ductile brittle transition (DBT) point by the traditional method of observing cracks. With the increase of penetration depth, pop-in will occur in the residual scratch depth of polished and ground silicon, indicating that the material removal mode has transformed, which provides an important basis for judging the DBT point. The DBT critical normal scratching force (38.93 mN) and residual scratch depth (−0.14 μm) of ground silicon are much higher than those of polished silicon, implying ground silicon is easier to achieve ductile processing. Meanwhile, when the penetration depth is the same, compared to polished silicon, the normal scratching force of ground silicon is generally larger. Finally, a single grain scratching SPH model of pre-stressed silicon is established. And the simulated phenomenon and conclusions are consistent with the experiment, which proves that the surface compressive stress is an important factor that causes the removal characteristics of ground silicon to be different from polished silicon. This study provides a theoretical basis for understanding the ultra-precision grinding removal mechanism of hard and brittle materials.

Characteristics of Silicon Substrates Fabricated Using Nanogrinding and Chemo-Mechanical-grinding

Mechanical effect of abrasives on silicon surface in chemo-mechanical grinding

Subsurface Structures of Monocrystalline Silicon Generated by Nanogrinding

Analysis on Ground Surface Damage of Quartz Fiber-Reinforced Quartz Composites

Investigation of machining mechanism of monocrystalline silicon in nanometric grinding

Effects of grinding speeds on the subsurface damage of single crystal silicon based on molecular dynamics simulations

Surface and subsurface cracks characteristics of single crystal SiC wafer in surface machining

Effect of grinding damage on cutting force and ductile machining during single grain scratching of monocrystalline silicon

AFM Tip-Based Fabrication of Silicon Nanostructures with Reduced Subsurface Amorphous Layers

Analytical modeling of grinding-induced subsurface damage in monocrystalline silicon

Mechanism analysis and process optimization of nanogrinding single-crystal SiC

Surface damage mechanism of monocrystalline silicon during single point diamond grinding

Atomistic understanding of the subsurface damage mechanism of silicon (100) during the secondary nano-scratching processing

AFM Analysis on Surface Roughness of Single Crystal Silicon Machined with Carbon Nanotubes Reinforced Composite Micro Grinding Wheel

A Molecular Dynamic Study of Nano-Grinding of a Monocrystalline Copper-Silicon Substrate

Surface Evolution and Stability Transition of Silicon Wafer Subjected to Nano-Diamond Grinding

Molecular Dynamics Study of Nano-Grinding Behavior for Silicon Wafer Workpieces with Nanoscale Roughness Under Diamond Abrasive Rotation and Translation

Ductile deformation and subsurface damage evolution mechanism of silicon wafer induced by ultra-precision grinding process

Study on micro-grinding mechanism and surface quality of hardened 20 vol% SiCp/Al composites

Surface Morphology Evolution during Chemical Mechanical Polishing Based on Microscale Material Removal Modeling for Monocrystalline Silicon

Generation and distribution of residual stress during nano-grinding of monocrystalline silicon