Abstract:Calcium hydroxide is a widely used bulk chemical, and traditional limestone calcination to prepare hydrated lime emits large amounts of CO2. Calcium carbide slag (CCS) is a waste residue with calcium hydroxide as the main component emitted by the PVC industry, which can be directly used to prepare calcium hydroxide. However, CCS has problems such as high impurity content, complex impurity occurrence state, and difficult separation. In this paper, the raw CCS and products under different separation conditions were prepared, and the presence state of main elements (Ca, Al, Si, Fe, C, Mg) in the CCS were studied by using XRD, XRF, XPS, SEM-EDS, and EPMA + SXES. According to the presence state of impurities, the microbubble strengthens in combination with agents used for deep directional separation of impurities in CCS, and DFT is used to calculate the surface binding energy between each component and agent in CCS. The results demonstrated that CaC2 and C wrap each other in CCS. Morphological and elemental chemical analyses of the dissociated residues revealed the existence of Si in the form of SiC and SiO2. Fe and C existed as particles of FeSi and carbon respectively. Al exists in the form of CaAl2O4 and Al2O3. Mg is loaded on the SiC in the form of Ca–Al–Mg mineral system. After the separation of microbubble equipment strengthens in combination with agents, the acid insoluble content can be reduced from 1.99% to 0.76%. At the same time, the yield can also reach 71.34%, and all indicators meet the standard indicators of industrial calcium hydroxide. The results can provide a new zero-carbon preparation pathway for calcium hydroxide.

Preparation of Light-weight Magnesium Oxide and Calcium Carbonate from Dolomite by Acidification:An Experimental Study

Study on Preparation of MgO Crystal Whisker from Magnesite

Preparation of Nano-sized Magnesium Hydroxide from Dolomites by Acid Immersing

Comprehensive Use of Dolomite-Talc Ore to Prepare Talc, Nano-Mgo and Lightweight CaCO3 Using an Acid Leaching Method

Study of Carbonizing Processes for Sintered Dolomite

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Preparation of Low-Cost Magnesium Oxychloride Cement Using Magnesium Residue Byproducts from the Production of Lithium Carbonate from Salt Lakes

Preparation and Characterization of Magnesium Hydroxide Nanoparticles from Dolomite-Talc Ore

Purification and Carbonation for High Loss and Low-Grade Diatomite in Inner Mongolia

Preparation of Magnesium Hydroxide Dry Powder by Hydrating Method

Preparation of Ccalcining MgO and its precursor

The Influence of Processing Conditions for the Preparation of Super-fine Hydroxide Magnesium by Hydrating Method

Additives Applied for Preparation of Superfine Mg(Oh)(2) Particles by Light-Burned Mgo at Low Temperature

Synthesis of Porous Rod-Like Basic Magnesium Carbonate Via Liquid Method

Preparation and Crystal Transformation Process of Magnesium Carbonate Hydrate Using MgSO4 as Raw Material

Improvement on the Processes of MgO Manufacture

Preparation of magnesium hydroxide by ammonia gas method

PARAMETER EFFECTS ON PREPARATION OF NANOSIZED PARTICLES OF MAGNESIUM HYDROXIDE FROM DOLOMITE AND THEIR CHARACTERS

Carbon emission free preparation of calcium hydroxide with calcium carbide slag (CCS) through micro-bubble impurities removal

The Preparation of Aluminum Hydroxide from High-Alumina Gangue Desilication Residues Based on Soda Lime Sintering Method

Preparation and characterization of anhydrous magnesium carbonate: Effect of different anions of the magnesium sources