Abstract:We fabricated ordered ZnO and nanowire arrays in anodic alumina membrane (AAM) by cathodic electrodeposition from a non-aqueous dimethylsulfoxide (DMSO) bath containing zinc chloride and dissolved oxygen. X-ray diffraction XRD), high-resolution transmission electron microcsopy (HRTEM), and electron diffraction (ED) show that the ZnO nanowires are well crystallized with wurtzite structure. The morphologies and structure of the ZnO nanowires have been characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results demonstrate that the ZnO nanowires with diameters of about 60nm are uniformly embedded into the hexagonally ordered nanopores of anodic alumina membrane. A sharp ultraviolet emission at 383nm and visible broad emission bands around 592nm were observed from ZnO nanowire arrays. They originated from the near-band emission due to the recombination of bound excitons and deep level emission due to defects, respectively. The cathodic electrodeposition technique in DMSO is also extended to synthesize CdO nanowire arrays.

Synthesis of Highly Ordered CdSe Nanowire Arrays Embedded in Anodic Alumina Membrane by Electrodeposition in Ammonia Alkaline Solution

Electrochemical Preparation of CdSe Nanowire Arrays

Non-Aqueous Cathodic Electrodeposition of Large-Scale Uniform Zno Nanowire Arrays Embedded in Anodic Alumina Membrane

Fabrication of Highly Ordered InSb Nanowire Arrays by Electrodeposition in Porous Anodic Alumina Membranes

Highly Ordered ZnS Nanowire Arrays Embedded in Anodic Alumina Membrane by a Hydrothermal Method with Double Diffusion

DC electrochemical deposition of CdSe nanorods array using porous anodic aluminum oxide template

Diameter- and current-density-dependent growth orientation of hexagonal CdSe nanowire arrays via electrodeposition.

Template Synthesis of CeO2 Ordered Nanowire Arrays

Porous CdS Nanowire Arrays Self-assembled in Anodic Aluminum Oxide Template

Silver Selenide Nanowires by Electrodeposition

Directional CdS Nanowires Fabricated by Chemical Bath Deposition

Single Crystal Ag7te4 Nanowire Arrays Prepared by Dc Electrodeposition from Aqueous Solution

Highly Ordered and Well-Oriented Single-Crystal Cdte Nanowire Arrays by Direct-Current Electrodeposition

Ordered Semiconductor CdO Nanowire Arrays: Synthesising by One-Step Low-Temperature Electrodeposition and Optical Properties

Template synthesis of single-crystal Cu nanowire arrays by electrodeposition

Preparation and Characterization of CdS Nanowire Arrays by Dc Electrodeposit in Porous Anodic Aluminum Oxide Templates

Photochemical Synthesis of Cdse and Pbse Nanowire Arrays on A Porous Aluminum Oxide Template

Fabrication and Structural Characterization of Large-Scale Uniform Sno2 Nanowire Array Embedded in Anodic Alumina Membrane

Direct Growth of CdSe Nanorods on ITO Substrates by Co-Anchoring of ZnO Nanoparticles and Ethylenediamine

Preparation of II-VI group semiconductor nanowire arrays by dc electrochemical deposition in porous aluminum oxide templates

A New Method to Prepare CdS Nanowire Arrays