Abstract:The nucleation and growth of colloidal CdSe nanocrystals with a variety of elongated shapes were explored in detail. The critical size nuclei for the system were magic sized nanoclusters, which possessed a sharp and dominated absorption peak at 349 nm. The formation of the unique magic sized nuclei in a broad monomer concentration range was not expected by the classic nucleation theory. We propose that this was a result of the extremely high chemical potential environment, that is, very high monomer concentrations in the solution, required for the growth of those elongated nanocrystals. The shape, size, and size/shape distributions of the resulting nanocrystals were all determined by two related factors, the magic sized nuclei and the concentration of the remaining monomers after the initial nucleation stage. Without any size sorting, nearly monodisperse CdSe quantum structures with different shapes were reproducibly synthesized by using the alternative cadmium precursors, cadmium-phosphonic acid complexes. A reasonably large excess of the cadmium precursor, which is less reactive than the Se precursor, was found beneficial for the system to reach the desired balance between nucleation and growth. The shape evolution and growth kinetics of these elongated nanocrystals were consistent with the diffusion-controlled model proposed previously. The branched nanocrystals had to grow at very high monomer concentrations because the multiple growth centers at the end of each branch must be fed with a very high diffusion flux to keep all branches in the 1D-growth mode. The rice-shaped nanocrystals were found as special products of the 3D-growth stage. The growth of the nanocrystals in the 1D-growth stage was proven to be not unidirectional after the length of the nanocrystals reached a certain threshold. Experimental results indicate that coordinating solvents and two ligands with distinguishable coordinating abilities are both not intrinsic requirements for the growth of elongated CdSe nanocrystals.

Self-Assembly of Semiconductor CdSe Nanocrystals by Bifunctional Linker Molecules

Room Temperature Self-Assembly of CdSe Nanocrystals on SiO2-coated Si Wafer

SELF-ASSEMBLY OF Ⅱ-Ⅳ COMPOUND NANOCRYSTALSON Si WAFER AT ROOM TEMPERATURE

Preparation of Nanochain and Nanosphere by Self-Assembly of Gold Nanoparticles

Synthesis and Isolatin of a Homodimer of Cadmium Selenide Nanocrystals

Size-, Shape-, and Assembly-Controlled Synthesis of Cu2−xSe Nanocrystalsvia a Non-Injection Phosphine-Free Colloidal Method

Direct fabrication of monodispersed ultrasmall CdS nanocrystals from self-assembled monolayers on Au(111) substrate

Self-assembly of charged microclusters of CdSe/ZnS core/shell nanodots and nanorods into hierarchically ordered colloidal arrays

Noninjection Synthesis of CdS and Alloyed CdS x Se 1−x Nanocrystals Without Nucleation Initiators

A Two-Step Synthetic Strategy Toward Monodisperse Colloidal Cdse and Cdse/Cds Core/Shell Nanocrystals

Nearly Monodisperse and Shape-Controlled CdSe Nanocrystals Via Alternative Routes: Nucleation and Growth.

Large-scale Synthesis of Nearly Monodisperse CdSe/CdS Core/shell Nanocrystals Using Air-Stable Reagents Via Successive Ion Layer Adsorption and Reaction.

A Dry Method To Synthesize Dendritic Ag2se Nanostructures Utilizing Cdse Quantum Dots And Ag Thin Films

Synthesis and self-assembly of CdSe nanometer scale building blocks

Self-assembly of CdS: from nanoparticles to nanorods and arrayed nanorod bundles

Manipulation of the Morphology of Cdse Nanostructures: the Effect of Si

Controlled Synthesis and Flexible Self-Assembly of Monodisperse Au@Semiconductor Core/Shell Hetero-Nanocrystals into Diverse Superstructures

Self-Assembled Colloidal Superparticles from Nanorods

Synthesis of Highly Ordered CdSe Nanowire Arrays Embedded in Anodic Alumina Membrane by Electrodeposition in Ammonia Alkaline Solution

Synthesis Of Cdse, Znse, And Znxcd1-Xse Nanocrystals And Their Silica Sheathed Core/Shell Structures

Electrochemical Preparation of CdSe Nanowire Arrays