Abstract:The nucleation and growth of colloidal CdSe nanocrystals with a variety of elongated shapes were explored in detail. The critical size nuclei for the system were magic sized nanoclusters, which possessed a sharp and dominated absorption peak at 349 nm. The formation of the unique magic sized nuclei in a broad monomer concentration range was not expected by the classic nucleation theory. We propose that this was a result of the extremely high chemical potential environment, that is, very high monomer concentrations in the solution, required for the growth of those elongated nanocrystals. The shape, size, and size/shape distributions of the resulting nanocrystals were all determined by two related factors, the magic sized nuclei and the concentration of the remaining monomers after the initial nucleation stage. Without any size sorting, nearly monodisperse CdSe quantum structures with different shapes were reproducibly synthesized by using the alternative cadmium precursors, cadmium-phosphonic acid complexes. A reasonably large excess of the cadmium precursor, which is less reactive than the Se precursor, was found beneficial for the system to reach the desired balance between nucleation and growth. The shape evolution and growth kinetics of these elongated nanocrystals were consistent with the diffusion-controlled model proposed previously. The branched nanocrystals had to grow at very high monomer concentrations because the multiple growth centers at the end of each branch must be fed with a very high diffusion flux to keep all branches in the 1D-growth mode. The rice-shaped nanocrystals were found as special products of the 3D-growth stage. The growth of the nanocrystals in the 1D-growth stage was proven to be not unidirectional after the length of the nanocrystals reached a certain threshold. Experimental results indicate that coordinating solvents and two ligands with distinguishable coordinating abilities are both not intrinsic requirements for the growth of elongated CdSe nanocrystals.

Synthesis and Isolatin of a Homodimer of Cadmium Selenide Nanocrystals

Self-Assembly of Semiconductor CdSe Nanocrystals by Bifunctional Linker Molecules

A Two-Step Synthetic Strategy Toward Monodisperse Colloidal Cdse and Cdse/Cds Core/Shell Nanocrystals

Noninjection Synthesis of CdS and Alloyed CdS x Se 1−x Nanocrystals Without Nucleation Initiators

Herstellung und Isolierung eines Homodimers aus CdSe-Nanokristallen

Colloidal synthesis of monodisperse quaternary CuInSSe nanocrystals

Synthesis of Highly Luminescent Mercaptosuccinic Acid-Coated Cdse Nanocrystals under Atmospheric Conditions

Nearly Monodisperse and Shape-Controlled CdSe Nanocrystals Via Alternative Routes: Nucleation and Growth.

Shape control of CdSe nanocrystals

Synthesis Of Cdse, Znse, And Znxcd1-Xse Nanocrystals And Their Silica Sheathed Core/Shell Structures

A solvothermal synthetic route to CdE (E = S, Se) semiconductor nanocrystalline

Alternative Routes Toward High Quality CdSe Nanocrystals

Large-scale Synthesis of Nearly Monodisperse CdSe/CdS Core/shell Nanocrystals Using Air-Stable Reagents Via Successive Ion Layer Adsorption and Reaction.

Aqueous Synthesis of Glutathione-Capped CdTe/CdS/ZnS and CdTe/CdSe/ZnS Core/Shell/Shell Nanocrystal Heterostructures

Organometallic Synthesis and Quantum Size Effect of Cdse Nanocrystallites

Synthesis of Cdse nanocrystals in aqueous solution

Spontaneous Transformation of CdSe Nanoparticles into Nonspherical Se Crystals: Role of the Precursor Ligand

Photochemical Synthesis and Characterization of CdSe Nanoparticles

Solvothermal Route to Nanocrystalline CdSe

Synthesis of tetrahedral quasi-type-II CdSe–CdS core–shell quantum dots

Solvothermal synthesis of nanocrystalline cadmium sulfide