Abstract:NiCoCrAlY+(6–8wt%)Y2O3 stabilized ZrO2(YSZ) two-layer thermal barrier coatings (TBCs) were deposited by electron beam physical vapor deposition on Ni3Al or Ni-base superalloy and their high temperature fatigue behavior was investigated experimentally and computationally. It has been found that the pre-treatment of the bond coat has greatly improved the thermal cyclic lifetime of TBCs with respect to those without pre-treatment. The lifetime is limited by the existence of interface between bond coat and top coat, and smoothing the interface can also improve the thermal cyclic lifetime. When the roughness of the interface changed from 3.76 to 0.82μm, testing lifetime increased from about 500 (1000 cycles) to 700h (1400 cycles), and the adhesive strength of the interface increased from 3.5 to 4.7MPam1/2 estimated from the result of surface Rock-well hardness testing. Cracks occurred in the thermally grown oxide (TGO) layer are considered to be the main reason for the failure of two-layer TBCs. It has been found that with pre-oxide layer thickness increasing from 1.0 to 3.0μm, the growth rate of TGO increased during thermal cyclic testing and the thermal cyclic lifetime of TBCs decreased from 730 to 450h. The lower lifetime was caused by the co-action of larger internal stress resulted from thicker TGO layer and the fatigue of the TGO layer. Finite element method (FEM) analysis showed that large tensile stress was introduced at the beginning of rapid cooling process, resulting in the spallation of top coat from bond coat. Ab initio calculation was carried out to evaluate the binding energy of the interface of bond coat and ceramic top coat, and FEM models were used to investigate stress and strain states in TBCs during thermal shock process as a function of cooling rate. The results showed that ZrO2/Ni interface exhibits nonmetallic properties, and that the chemical bonding in ZrO2/Ni is covalent–ionic in nature. The calculation of binding energies between both Ni and O and Zr and O indicates that the binding energy of Ni and O is larger than that of Zr and O, which is helpful to investigate the failure mechanism of thermal barrier coatings.

Sintering and Failure Behaviour of Eb-Pvd Thermal Barrier Coating after Isothermal Treatment

Microstructural evolution of plasma spray physical vapor deposited thermal barrier coatings at 1150 °C studied by impedance spectroscopy

Effect of Heat Treatment at 900 °C on Microstructural and Mechanical Properties of Thermal Barrier Coatings

Failure behaviour of EB-PVD YSZ thermal barrier coatings under simulated aero-engine operating conditions

Effect Of Thermal Exposure On The Microstructure And Properties Of Eb-Pvd Gradient Thermal Barrier Coatings

Preparing and Study of EB-PVD Thermal Barrier Coatings on Titanium Substrates

Thermal cycling of EB-PVD TBCs based on YSZ ceramic coat and diffusion aluminide bond coat

Study of Failure of EB-PVD Thermal Barrier Coating Upon Near-Α Titanium Alloy

Investigation of the failure mechanism of thermal barrier coatings prepared by electron beam physical vapor deposition

Characterization and Evaluation of EB-PVD Thermal Barrier Coatings by Impedance Spectroscopy

Infrared Radiative Properties of EB-PVD Thermal Barrier Coatings

Thermophysical properties and thermal cycling behavior of plasma sprayed thick thermal barrier coatings

Effect of sintering temperature on microstructure and properties of thermal barrier coating

Novel Microstructure of EB-PVD Double Ceramic Layered Thermal Barrier Coatings

Structure and Performance of YSZ Thermal Barrier Coatings Irradiated by High Intensity Pulsed Ion Beam

Failure Characteristics and Life Prediction for Thermally Cycled Thermal Barrier Coatings

Experimental and computational study on hot fatigue process of thermal barrier coatings by EB-PVD

Preparation and High Temperature Oxidation Resistance of Thermal Barrier Coatings on Ti-Al Alloys by EB-PVD

Effect of Surface Strengthening on High Temperature Oxidation and Bonding Strength of EB-PVD Thermal Barrier Coating

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

GdYbZrO thermal barrier coatings by EB-PVD: Phase, microstructure, thermal properties and failure