Abstract:Atmospheric plasma sprayed thick thermal barrier coatings (TBCs), comprising of 1.5 mm thickness yttria stabilized zirconia (YSZ) coating, have been developed for increasing thermal protection of combustor applications. Different segmentation crack densities of the YSZ coating were created by controlling the deposition conditions. It was found that the substrate temperature played a dominant role in determining the segmentation crack density. The density was found to increase with the increase of substrate temperature and liquid splat temperature. High passage thickness, if achieved by low plasma gun speed, contributed to improve the segmentation crack density. The density could not be effectively improved by increasing the powder feed rate, although a high passage thickness was obtained in this case. The pores, mainly consisting of delaminations with the radii range between 0.02 and 1 μm, prevent the segmentation cracks from propagation. The coatings sprayed at high substrate temperature show an excellent intersplat bonding and often even continuous columnar grains through several splats. Additionally, horizontally branching cracks were also formed together with the segmentation cracks when a high lamellar thickness was used during the spraying. Thermal cycling tests showed that the coating with a segmentation crack density of approximately 3.6 mm−1 had a lifetime of more than 1700 cycles at 1238 °C (surface)/938 °C (bond coat), indicative of excellent thermal shock resistance. Failure of the TBCs occurred by chipping in the surface layer of YSZ coating, which is different from the traditional interface delamination failure occurred with thinner TBCs.

Thermophysical properties and thermal cycling behavior of plasma sprayed thick thermal barrier coatings

Atmospheric Plasma Sprayed Thick Thermal Barrier Coatings with High Segmentation Crack Density

Microstructure and Thermal Properties of Plasma Sprayed Thermal Barrier Coatings from Nanostructured YSZ

Thermal Stability of Plasma-Sprayed Thick Thermal Barrier Coatings Using Triplex ProTM-200 Torch

Segmentation Cracks in Plasma Sprayed Thin Thermal Barrier Coatings

THERMAL SHOCK BEHAVIOR OF AIR PLASMA SPRAYED CoNiCrAlY/YSZ THERMAL BARRIER COATINGS

Thermal Cycling Failure Mechanism of TBCs Sprayed by High Energy Plasma Spraying

Thermal shock behaviors of YSZ thick thermal barrier coatings fabricated by suspension and atmospheric plasma spraying

Microstructure, Thermal Conductivity and Thermal Cycling Behavior of Thermal Barrier Coatings Prepared by Plasma Spray Physical Vapor Deposition

A Novel Plasma-Sprayed Durable Thermal Barrier Coating with a Well-Bonded YSZ Interlayer Between Porous YSZ and Bond Coat

Microstructural evolution of plasma spray physical vapor deposited thermal barrier coatings at 1150 °C studied by impedance spectroscopy

Thermal shock behavior of air plasma sprayed thermal barrier coatings under high temperature wind tunnel

Structure–property differences between supersonic and conventional atmospheric plasma sprayed zirconia thermal barrier coatings

Cracking Behavior of Gd2Zr2O7/YSZ Multi-Layered Thermal Barrier Coatings Deposited by Suspension Plasma Spray

Thermal properties of plasma-sprayed thermal barrier coating with bimodal structure

Microstructural Design and Properties of Supersonic Suspension Plasma Sprayed Thermal Barrier Coatings

Thermal Cycling Behavior of Nanostructured and Conventional Yttria-Stabilized Zirconia Thermal Barrier Coatings Via Air Plasma Spray

Internal Diameter Atmospheric-Plasma-Sprayed High-Performance YSZ-Based Thermal Barrier Coatings

Wide-velocity Range High-Energy Plasma Sprayed Yttria-Stabilized Zirconia Thermal Barrier Coating — Part II: Structural Defects and Thermal-Bonding Properties

Phase Stability, Fracture Toughness and Thermal Cycling Behavior of Supersonic Suspension Plasma Sprayed Scandia-Yttria Co-doped Zirconia Thermal Barrier Coatings

Thermal shock performance and failure behavior of Zr6Ta2O17-8YSZ double-ceramic-layer thermal barrier coatings prepared by atmospheric plasma spraying