Abstract:Thermal barrier coatings (TBCs) are extensively used in gas turbine engines in power generation and aerospace applications. Improvements in TBC performance and lifetime are continuously pursued by the gas turbine industry. Suspension plasma spraying (SPS) has shown promising results in recent years as it could produce a porous columnar TBC microstructure exhibiting low thermal conductivity and high durability. Further improvements in lifetime and fundamental understanding of failure mechanisms would lead to their wider application. Lifetime of a TBC system is dependent not only on the topcoat microstructure and chemistry, but also on topcoat-bondcoat interface and bondcoat characteristics as they influence the growth rate of thermally grown oxide (TGO) layer as well as the mismatch stresses generated in the topcoat during operation. Moreover, in SPS TBCs, the column density and porosity in the topcoat are also affected by the bondcoat surface roughness which in turn affects TBC lifetime. In previous work, it was shown that bondcoat surface treatment by shot peening followed by light grit blasting can significantly enhance the cyclic lifetime of SPS TBCs. The objective of this work was to gain further insight into the lifetime improvements due to surface treatment of bondcoat. Commercial NiCoCrAlY powder was deposited by high velocity air fuel (HVAF) and high velocity oxy fuel (HVOF) spraying while SPS was used to deposit yttria stabilised zirconia topcoat. Before spraying the topcoat, the bondcoat samples were subjected to vacuum heat treatment, shot peening, and/or grit blasting. Residual stress measurements were performed by X-ray diffraction on samples with different variants of bondcoat treatments and compared with Almen strip tests. The lifetime was examined by thermal cyclic fatigue testing. The relationships between changes in bondcoat surface roughness, residual stress state and microstructure due to surface treatments, and resultant topcoat microstructure and lifetime were studied and discussed.

Effect of Surface Strengthening on High Temperature Oxidation and Bonding Strength of EB-PVD Thermal Barrier Coating

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

Influence factors of high temperature oxidation for Pt-modified-aluminide bond coatings

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

TGO stress growth for Pt-modified aluminide bond coats during high temperature oxidation

Thermal cycling of EB-PVD TBCs based on YSZ ceramic coat and diffusion aluminide bond coat

Formation and Behavior of Thermal Barrier Coatings on Nickel-Base Superalloys

Effect of Shot Blasting on NiCrAlY Bonding Coating of Thermal Barrier Coatings

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

Effect of Heat Treatment at 900 °C on Microstructural and Mechanical Properties of Thermal Barrier Coatings

Characterisation and Oxidation Behaviour of Plasma Surface Alloyed on Γ-Tial Alloy

The effect of temperature and roughness of the substrate surface on the microstructure and adhesion strength of EB-PVD ZrO2-%8wtY2O3 coating

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Failure behaviour of EB-PVD YSZ thermal barrier coatings under simulated aero-engine operating conditions

The Effect of Shot Blasting Abrasive Particles on the Microstructure of Thermal Barrier Coatings Containing Ni-Based Superalloy

Superior toughness of thermal barrier coating caused by co-doping of trivalent and pentavalent oxides

High‐temperature oxidation and TGO growth behavior of Sr.9(Zr.9Yb.05Y.05)O2.85 thermal barrier coatings

Enhancing the Oxidation Resistance of NiCrAlY Bond Coat by High-Current Pulsed Electron Beam Irradiation

Structural evolution and enhanced thermal cycling life of HVAF-sprayed NiCrAlY bond coat modified by YSZ

Understanding the effect of bondcoat surface treatment on enhanced lifetime of suspension plasma sprayed thermal barrier coatings

Effects of a nano carbide coating fabricated by EB-PVD on the interfacial stability of aluminide coated superalloy