Effect of sintering temperature on microstructure and properties of thermal barrier coating

Erjuan Yang,Taijiang Li,Wei Li,Yong Li,Gang Liu

DOI: https://doi.org/10.13251/j.issn.0254-6051.2017.10.034

2017-01-01

Abstract:Because the sintering phenomenon of thermal barrier coating is hardly avoided in the service process at high temperature, the failure of the coating is easily happened. High temperature sintering test was carried out on the YSZ coating, which was prepared by plasma spraying, to study the evolution law of microstructure and mechanical properties at 1000, 1100, 1200 and 1300 ℃ for different time, respectively. The results show that the cross-sectional microstructures of YSZ coating after 500 h sintering treatment are similar to the as-sprayed one. The porosity is in the overall downward trend, and the early stage (0-50 h) decline rate is much higher than that of the subsequent heat preservation stage. As a whole, the porosity of coating deceases gradually, which ranging from 12% to 14% after sintering for a long time. The growth rate of elastic modulus and micro-hardness of coating in the early stages (0-50 h) are much higher than those of subsequent sintering process. And with the sintering temperature increasing, the extent of elastic modulus and micro-hardness of coating increasing is larger, and the rapidly increasing stage gets shorter.