Abstract:Microstructural modifications of a thermally sprayed MCrAlY bond coat subjected to high-current pulsed electron beam (HCPEB) and their relationships with thermal cycling behavior of thermal barrier coatings (TBCs) were investigated. Microstructural observations revealed that the rough surface of air plasma spraying (APS) samples was significantly remelted and replaced by many interconnected bulged nodules after HCPEB irradiation. Meanwhile, the parallel columnar grains with growth direction perpendicular to the coating surface were observed inside these bulged nodules. Substantial Y-rich Al2O3 bubbles and varieties of nanocrystallines were distributed evenly on the top of the modified layer. A physical model was proposed to describe the evaporation-condensation mechanism taking place at the irradiated surface for generating such surface morphologies. The results of thermal cycling test showed that HCPEB-TBCs presented higher thermal cycling resistance, the spalling area of which after 200 cycles accounted for only 1% of its total area, while it was about 34% for APS-TBCs. The resulting failure mode, i.e., in particular, a mixed delamination crack path, was shown and discussed. The irradiated effects including compact remelted surface, abundant nanoparticles, refined columnar grains, Y-rich alumina bubbles, and deformation structures contributed to the formation of a stable, continuous, slow-growing, and uniform thermally grown oxide with strong adherent ability. It appeared to be responsible for releasing stress and changing the cracking paths, and ultimately greatly improving the thermal cycling behavior of HCPEB-TBCs.

Preparing and Study of EB-PVD Thermal Barrier Coatings on Titanium Substrates

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Thermal cycling of EB-PVD TBCs based on YSZ ceramic coat and diffusion aluminide bond coat

Performance of TBCs system due to the different thicknesses of top ceramic layer

Thermal Cycling Behavior of Thermal Barrier Coatings with MCrAlY Bond Coat Irradiated by High-Current Pulsed Electron Beam

Formation and Behavior of Thermal Barrier Coatings on Nickel-Base Superalloys

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

Failure behaviour of EB-PVD YSZ thermal barrier coatings under simulated aero-engine operating conditions

The Microstructural Investigation of Vermiculite-Infiltrated Electron Beam Physical Vapor Deposition Thermal Barrier Coatings

Failure Mechanism of EB-PVD Thermal Barrier Coatings under the Synergistic Effect of Thermal Shock and CMAS Corrosion

Enhancing the performances of EB-PVD TBCs via overlayer Al-modification

Isothermal Oxidation Behavior of VC and Columnar Structured Thermal Barrier Coatings Deposited by Suspension Plasma Spray Technology

Effect of Heat Treatment at 900 °C on Microstructural and Mechanical Properties of Thermal Barrier Coatings

Microstructure evolution of Al-modified 7YSZ PS-PVD TBCs in thermal cycle

Thermal shock behaviors and failure mechanisms of EB-PVD thermal barrier coatings using radiant heating

Study on Construction Mechanism of Ceramic–Metal Thermal Barrier Coating System by Plasma Spraying

Isothermal and Cyclic Oxidation Performance of Vertically Cracked and Columnar Thermal Barrier Coating Structures Produced Using Axial Suspension Plasma Spraying Process

Microstructural Characterization and Thermal Barrier Effects of Conventional and Nanostructured Zro2-7wt.%Y2o3 Thermal Barrier Coatings Deposited by Plasma Spraying

Performance and Failure Modes of Thermal Barrier Coatings Deposited by EB-PVD on Blades under Real Service Conditions in Gas Turbine

Performance of Atmospheric Plasma-Sprayed Thermal Barrier Coatings on Additively Manufactured Super Alloy Substrates