Abstract:The precipitates in a Mg-7Gd-5Y-1Nd-0.5Zr alloy aged to peak-ageing plateau (aged at 210 degrees C from 18 h to 180 h) were studied using transmission electron microscopy (TEM), high-resolution TEM (HRTEM) and high-angle annular detector dark-field scanning transmission electron microscopy (HAADF-STEM). Precipitation at the peak-ageing plateau involves the formation of the beta' phase and a new type of plate-shaped phase precipitated along the (0 0 0 1)(alpha) habit plane. The ellipsoid morphology of beta' was illustrated according to [0 0 0 1](alpha) and [1 0 (1) over bar 0](alpha) zone axes observations. The orientation relationship between the beta' precipitates and matrix satisfies [0 0 1](beta')//[0 0 0 1](alpha) and (1 0 0)(beta')//(1 1 (2) over bar 0)(alpha), respectively. The TEM and HRTEM results indicate that the beta' precipitates have a base-centred orthorhombic structure with lattice parameters a = 0.64 nm, b = 2.22 nm and c = 0.52 nm. Further, atomic-scaled HAADF-STEM observations suggest a Mg7RE-type and not a Mg15RE-type structure for the beta' phase. The positive thermal stability of the alloy at 210 degrees C ageing is attributed to the coherent relationship with the matrix and the formation of an interlaced network of the beta' precipitates. Aside from the beta' phase, a large amount of precipitate particles were observed to form on the (0 0 0 1)(alpha) habit plane in the peak-aged samples. The new type of precipitates have a plate shape, of approximately 5 nm wide along the [1 0 (1) over bar 0](alpha) direction of the matrix and approximately 5 nm long along the [(2) over bar 1 1 0](alpha) direction. A completely coherent relationship with the matrix can also be observed. (c) 2013 Elsevier B.V. All rights reserved.

Precipitates Formed in a Mg–7Y–4Gd–0.5Zn–0.4Zr Alloy During Isothermal Ageing at 250 °C

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Precipitation in a Mg–10Gd–3Y–0.4Zr (wt.%) Alloy During Isothermal Ageing at 250 °C

Effect of Ageing Treatment on the Precipitation Behaviour of Mg–Gd–Y–Zn–Zr Alloy

Precipitate Evolution in Mg−7Gd−3Y−1Nd−1Zn−0.5Zr Alloy During Isothermal Ageing at 240 °C

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Precipitate evolution of as-cast Mg-9Gd-2Y-0.5Zn-0.5Zr alloy containing LPSO, β′′, β′ and γ'' phases during isothermal aging at 200 °C

Ageing Behavior of Extruded Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr (wt.%) Alloy Containing LPSO Phase and Γ′ Precipitates

Precipitation Processes During the Peak-Aged and Over-Aged Stages in an Mg-Gd-Y-Zr Alloy

The Aging Behaviour of a Mg-10Gd-3Y-1.0Zn-0.5Zr (wt.%) Alloy with Long-Period Stacking Ordered Phase at 275°C

Microstructure and Mechanical Properties of an Extruded Mg-2Dy-0.5Zn Alloy

TEM study on the microstructural evolution in an Mg–Y–Gd–Zn alloy during ageing

Microstructure Evolution in a Mg–15Gd–0.5Zr (wt.%) Alloy During Isothermal Aging at 250°C

Precipitation Behavior of Mg-7Gd-3Y-2Zn-0.5Zr Alloy during Isothermal Aging

Effect of Ageing Treatment on the Microstructure, Texture and Mechanical Properties of Extruded Mg–8.2Gd–3.8Y–1Zn–0.4Zr (wt%) Alloy

Effect of Y on Age Hardening Response and Mechanical Properties of Mg-xY–1.5LPC −0.4zr Alloys

Characterisation of Precipitates in a Mg–7Gd–5Y–1Nd–0.5Zr Alloy Aged to Peak-Ageing Plateau

Effect of precipitates on microstructures and properties of forged Mg-10Gd-2Y-0.5Zn-0.3Zr alloy during ageing process

Precipitation Behavior and Mechanical Properties of a Mg–Zn–Y–Zr Alloy Processed by Thermo-Mechanical Treatment

Precipitates formed in the as-forged Mg–Zn–RE alloy during ageing process at 250°C

Evolution of precipitates in Mg?7Gd?3Y?1Nd?1Zn?0.5Zr alloy with fine plate -like 14H-LPSO structures aged at 240?C