Effect of Ageing Treatment on the Microstructure, Texture and Mechanical Properties of Extruded Mg–8.2Gd–3.8Y–1Zn–0.4Zr (wt%) Alloy

Y. Q. Chi,M. Y. Zheng,C. Xu,Y. Z. Du,X. G. Qiao,K. Wu,X. D. Liu,G. J. Wang,X. Y. Lv

DOI: https://doi.org/10.1016/j.msea.2012.11.125

2013-01-01

Abstract:Extruded Mg–8.2Gd–3.8Y–1Zn–0.4Zr (wt%) alloy was subjected to ageing treatment at 200°C. The microstructures, textures and mechanical properties of the as-extruded and peak-aged alloys were investigated. Recrystallization occurred during ageing treatment. A large number of β′ phases were observed in the peak-aged alloy, accompanied with the decrease of the volume fraction of LPSO phases. A basal fiber texture and an unusual texture component with basal planes perpendicular to the extrusion direction were found in the as-extruded alloy, and the basal fiber texture was strengthened after ageing treatment. The peak-aged alloy exhibited a tensile yield strength (TYS), an ultimate tensile strength (UTS) and an elongation to failure of 395MPa, 470MPa and 8%, respectively, at ambient temperature, and 271MPa, 311MPa and 19%, respectively, at 300°C. The superior strength of the peak-aged alloy was mainly attributed to the precipitation of fine β′ phases, the remaining LPSO phases and the texture modification.