Synthesis, investigation of temperature and salt resistant polyacrylamide microspheres used for deep sealing and profile control and function strengthening mechanism
Huo Jinhua,Zhang Siman,Liu Junwei,Wei Chenxi,Zhang Ruizhi,Zhang Xing,Li Shanjian
DOI: https://doi.org/10.1002/app.55620
IF: 3
2024-04-28
Journal of Applied Polymer Science
Abstract:The MAH structural unit contains a rigid circular structure, and S‐CaCO3 can act as a nucleating agent and reaction center, which can reduce the collapse and degradation of the polymer collective. Based on the requirements of deep sealing and profile control for the excellent temperature and salt resistance on polyacrylamide microspheres, the Poly‐AM/AMPS was prepared depends on aqueous solution polymerization method to improving oil and gas recovery efficiency in low‐permeability and heterogeneous reservoirs resulted by water channeling. The key technical parameters were established through single‐factor experimental methods, and the chemical structure was studied by infrared spectrum analysis (FTIR), energy spectrum analysis, and x‐ray diffraction analysis, and then the thermal stability was investigated depends on the thermogravimetric (TG) and differential thermogravimetric (DTG) distribution curves, moreover, the particle size and distribution, microstructure, and surface morphology were further studied. As a result, the results confirmed that the molecular structure of Poly‐AM/AMPS meets the expected design, and the quality retention rate at 800°C is 17.4%, the median particle size of Poly‐AM/AMPS particles is 35.88 μm, and the particle size distribution range is about 1.94–497.8 μm. Further, the Poly‐AM/AMPS was modified by maleic anhydride, sodium styrenesulfonate, and dimethyl diallyl ammonium chloride through conventional functional strengthening and modification, modified by nano‐SiO2, GO, and S‐CaCO3 through nano‐functional strengthening and modification. Additionally, the functional strengthening and modification mechanism was studied depends on the FTIR, TG, and DTG methods.
polymer science