Abstract:Titanium carbide, titanium carbonitride or titanium nitride were synthesized by a two-step carbothermic reduction method. In this method, a single-phase precursor TiCnO1-n was firstly prepared from the reaction between titanium dioxide and carbon black in argon atmosphere. Then, the precursor was used as raw materials to prepare TiN, TiCxN1-x or TiC. For the production of TiN or TiCxN1-x, the precursor was further carbothermally reduced and nitrided in nitrogen gas atmosphere. For the production of TiC, the precursor was further reduced by carbon in vacuum. In the first reduction step, it was hard to determine the precise molar ratio of TiO2:C due to the uncontrollable ratio of gaseous products CO and CO2 from TiO2 to TiCnO1-n. Whereas the second step only took place in the high temperature region and the gaseous products were thermodynamically in favor of CO. Therefore, the expected products can be obtained by precisely controlling the carbon addition after analyzing the contents of carbon and oxygen in TiCnO1-n. High purity products were prepared with good dispersivity, narrow size distribution and controllable atomic ratio of C:N. The effects of reduction temperature, reaction time, ball milling and particle sizes of raw material TiO2 were studied in detail. TiN, TiCxN1-x and TiC could be obtained under the same optimum time and temperature of 1773 K for 4 h in first step and 1873 K for 8 h in second step.

Research Progress of Silicon Nitride Prepared by Carbothermal Reduction Method

Porous Silicon Nitride Ceramics Prepared by Carbothermal Reduction Method

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Porous Silicon Nitride Ceramics Prepared by Reduction-Nitridation of Silica

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Silicon Nitride :Preparation and Current Research on Growth Kinetics

Porous Silicon Nitride Ceramics Prepared by Reduction – Nitridation of Diatomite

Synthesis of monodisperse and high-purity α-Si3N4 powder by carbothermal reduction and nitridation

Porous Silicon Nitride Ceramics Fabricated by Carbothermal Reduction-Reaction Bonding

Progress in Preparation and Properties of Porous Silicon Nitride Ceramics

Theoretical and experimental study of the mechanism for preparation of SiC nanowires by carbothermal reduction

Biomimetic Synthesis of Porous Si_3N_4 Ceramics

Research Progress of Porous Silicon Nitride Ceramics

Biomorphic Silicon Nitride Ceramics with Fibrous Morphology Prepared by Sol Infiltration and Reduction–Nitridation

Effect of Sintering Conditions on the Formation of SiC Nanomaterials in Carbothermal Reduction

Synthesis of aluminum nitride fibres from aluminum silicate fibres by carbothermal reduction method

Preparation of SiC Powders by Carbothermal Reduction with Bamboo Charcoal As Renewable Carbon Source

Research of Silicon Nitride Powder Prepared by Self-propagating High-temperature Synthesis

Preparations of Titanium Nitride, Titanium Carbonitride and Titanium Carbide Via a Two-Step Carbothermic Reduction Method

Synthesis of TiN-Si3N4 Composites from Rutile and Quartz by Carbothermal Reduction Nitridation

Progress in Research and Application of Gas-Pressure-Sintered Silicon Nitride Ceramics