Abstract:Traditional TiN coatings cannot meet the requirements in many applications under extreme conditions because of their relatively low hardness (similar to2000Hv), high friction coefficient (>0.4), inade- quate thermal stability and insufficient corrosion. (Ti,Al)N coatings are a promising alternative to TiN coatings, which have recently been obtained by some groups. However, The deposition of coatings on ceramic substrates prepared by traditional physical vapor deposition was puzzled by low adhesions. In this work, (Ti,Al)N deposition was realized by a new technique namely pulsed high energy density plasma. The ratio of Ti and Al atoms was kept constant at 1:1, since this was known to be the best ratio for (Ti,Al)N synthesis. However, the process allows many other deposition parameters to be varied. In this study, the influences of the discharge voltage between the inner and outer electrode, the distance between the sample and the pulsed plasma gun, and the shot number of the pulsed plasma on coating formation and properties were investigated. Under the optimum deposition conditions, the adhesive strength of (Ti,Al)N coating to Si3N4 ceramic substrate was satisfactory with the critical load up to more than 80 mN. In addition, the coatings were investigated with respect to mechanical and wear behavior, including nanohardness, Young's modulus and cutting performances. The (Ti,Al)N coatings possess resulted very high values of nanohardness and Young's modulus, which are near to 40 GPa and 680 GPa, respectively. Because of the deposition of (Ti,Al)N coatings the wear resistance and edge life of the coated tools were improved dramatically evaluated by the cutting perforinances of the coated tools in turning HT250 (HB230) steel under industrial conditions. These improvements were attributed to a combination of four effects of deposition, ion implantation, quench and solid solution strengthening in terms of the structural analyses.

Wear Resistance of Arc Ion Plating Deposited TiN/AlN-TiAlN Film

Evaluation of wear resistance of CrN, CrAlN, and TiAlN coatings deposited by multi-arc ion plating on spinning die of Cr12MoV

Tribological Performances of TiAlN Film on TC4 Alloy Surface Prepared by Two Kinds of Arc Target

Thermal Fatigue and Oxidation Resistance of TiAlN Coating Grown by Arc Ion Plating

High Temperature Behavior of TiAlN Coating Prepared by Arc Ion Plating on TC4 Titanium Alloy

High Temperature Protection Properties of TiAlN Coating Prepared by Arc Ion Plating on Surface of Ti6Al4V Titanium Alloy

Tribological Behaviors of Super-Hard TiAlN Coatings Deposited by Filtered Cathode Vacuum Arc Deposition

Phase Composition, Hardness, and Thermal Shock Properties of AlCrTiN Hard Films with High Aluminum Content

High Temperature Sliding Wear Behaviors of Ion Plating Tin Composite Coating with Ion Nitriding As Interlayer on Hot Work Die Steel

Tribological properties of Ti-N compound layer formed on Ti6Al4V by HCD assisted plasma nitriding

Characterization of Ti-Al-N Films Deposited by Cathodic Vacuum Arc with Different N2 Partial Pressure

Properties of TiAlCrN coatings prepared by vacuum cathodic arc ion plating

Characterization of Superhard Ternary (ti,al)n Coatings Prepared by Pulsed High Energy Density Plasma

Structure and Wear Resistance of the Multi-Arc Ion Plated Coating on TC11 Alloy

Tribological Properties and Preparation of (Ti,Al)N Coatings on High Speed Steel Substrate

Microstructures and properties of (TiCrZrVAl)N high entropy ceramics films by multi-arc ion plating

Wear Behavior of TiN/TiAlSiN Nanocomposite Multilayer Coatings from Ambient Temperature to Medium Temperature

Thermal and Thermo-Mechanical Properties of Ti–Al–N and Cr–Al–N Coatings

Microstructural response and wear behaviour of Ti-6Al-4V impregnated with Ni/Al2O3 + TiO2 nanostructured coating using an electric arc

Investigation of Hardness, Tribological and Adhesion Properties of TiAlNiVN HEA Films Heat Treated at Different Temperatures

Fabrication and Performance of TiN/TiAlN Nanometer Modulated Coatings