Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Effect of Different Types of Surfactants on Properties of Ceria-Zirconia Solid Solutions

Effects of ceria/zirconia ratio on properties of mixed CeO2-ZrO2-Al2O3 compound

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Effects of Surfactants on the Pore-forming of Ce0.27Zr0.18Y0.025La0.025Al0.5Ox Prepared by Coprecipitation Method

Synthesis and Characterization of Mesostructured Ceria-Zirconia Solid Solution

Hydrothermal Preparation of Mesoporous Ce0.5Zr0.5O2 Solid Solution with High Surface Area by PEG Template

Synthesis of Nanostructured Ceria, Zirconia and Ceria–zirconia Solid Solutions Using an Ultrahigh Surface Area Carbon Material As a Template

Influence of Surfactant on Performance of CeZrYO Oxygen Storage Material

Preparation of ceria-zirconia solid solution with enhanced oxygen storage capacity and redox performance

Facile Synthesis of High Surface Area Nanostructured Ceria-Zirconia-yttria-lanthana Solid Solutions with the Assistance of Lauric Acid and Dodecylamine

Aluminum-doped ceria-zirconia solid solutions with enhanced thermal stability and high oxygen storage capacity.

Preparation and property investigation of CeO2–ZrO2–Al2O3 oxygen-storage compounds

Preparation of High Oxygen Storage Capacity and Thermally Stable Ceria–zirconia Solid Solution

Preparation of Mesoporous Ce0.5Zr0.5O2 Mixed Oxide by Hydrothermal Templating Method

Preparation and characterization of high specific surface area Ce 0.5Zr0.5O2 mixed oxide

Mesoporous Yttria-Zirconia Solid Solution with Improved Textural Properties Prepared Via Lauric Acid-Assisted Synthesis

Characterization of Cerium-Zirconium Solid Solutions Prepared by the Microwave-Assisted Approach

Hydrothermal synthesis of tin doped ceria-zirconia solid solutions with enhanced thermal stability and oxygen storage capacity

Surface and Texture Properties of Tb-Doped Ceria-Zirconia Solid Solution Prepared by Sol-Gel Method

Synthesis and Characteristics of La Doped Ceria–Zirconia Composite with Uniform Nano-Crystallite Dispersion

Preparation of Ceria-Zirconia Solid Solution by Urea-Based Hydrothermal-Copricipitation Method and its Catalytic Application