Abstract:Low-cost thermal insulation porous ceramics with uniform pore diameter and low bulk density were prepared with soda-ash dregs and felsic tailings. We investigated the effect of temperature, foaming agent, fluxing agent, Al 2 O 3 and CaO content on the pore structure and crystal phase of porous ceramics. The effect of Ca 2+ in soda-ash dregs on the preparation of quartz-feldspar based porous ceramics was studied. The results showed that the contribution of Ca 2+ to the preparation of porous ceramics in this system was mainly to accelerate the Si-O bond fracture and reduce the sintering temperature at the initial stage of sintering, which destroyed the needle-like feldspar in the high temperature melt and reduced the melt viscosity, thus reduced the foaming resistance and promoted the porous products with uniform pore size distribution. The Ca 2+ content on the high side can participate in the formation of crystals in sintering. The generated needle-like diopside and augite, which have small length-diameter ratio, will negligibly change in the viscosity of melt at high temperatures, and their inhibition effect on pores is not as good as that of feldspar with large length-diameter ratio, resulting in the merger and collapse of pores. But the increase of diopside and augite can improve the compressive strength of porous products to some extent. Porous ceramic products containing needle-like feldspar phase can be prepared by using two kinds of solid waste, which can improve the compressive strength of the products and reduce the raw material cost and energy consumption while comprehensively utilizing the double solid waste. The optimal product has a bulk density of 0.45 g/cm 3 , a compressive strength of 3.17 MPa, and a thermal conductivity of 0.11 W/(m·K).

Studies on the Sintering Process of High Pure BeO Ceramics with High Thermal Conductivity

Effects of Sintering Techniques on the Microstructure and Performance of High Purity Beryllium Oxide Ceramics

Impact of the Mineral Composition and Sintering Temperature on the Synthesis of Anorthite Ceramics

Influence of CaO content by mass in sintering aid and sintering temperature on the properties of Al2O3-based microwave ceramic materials

Study on Sintering Additive for High Purity Beryllium Oxide Ceramics with High Thermal Conductivity

Microstructure and Properties of SiO2-doped High Pure Beryllium Oxide Ceramics

Hot-pressing of BeO Ceramics and Its Thermal Conductivity and Flexural Strength

Low sintering shrinkage and high strength of porous mullite–zirconia ceramics: Effect of AlF3 and ZrSi2 contents

The Influence of Rare Earth Dopants upon Properties of High Purity Beryllium Oxide Ceramics

Observation on the ceramic powder evolution during sintering by synchrotron radiation X-ray computed tomography

Study on Sintering Kinetic Curves of BaTiO3 Ceramics

Low temperature firing of BiSbO4 microwave dielectric ceramic with B2O3–CuO addition

Influence of B4C Additive on Sintering and Crystallization of Fused Silica Ceramics

Effect of Sintering Temperature on Properties of Porous SiC Ceramics Produced Through Coat-mix/Composite Additives Process

Preparation of Thermal Insulation Ceramics Using Felsic Tailings as Main Raw Material and Soda-ash Dregs as Flux

Research on Sintering Property of CaO-B2O3-SiO2 System Glass Ceramics

Fabrication of Si3N4 Ceramics with High Thermal Conductivity and Flexural Strength Via Novel Two-Step Gas-Pressure Sintering

Effect of B2O3 Addition on Low-temperature Sintering Behavior and Properties of SiC/h-BN Multiphase Ceramics

Effect of BPO4-B2O3 Composite Additive on Crystallization and Sintering of Silica Ceramics

Effect Of Sintering Process On Micro-structure And Properties Of Mullite Porous Ceramics Containing magnesium oxide

Study on Porous Mullite Ceramic Material Based on Orthogonal Experimental Method