Influence of B4C Additive on Sintering and Crystallization of Fused Silica Ceramics

Yan,Wenchao,Yuanyuan Wang,Shixiong Min,Xinke Xiao,Jianzhong,Jinbo,Xia,Feng

2013-01-01

Abstract:The green bodies were prepared by adding B4C （0.5%,1.5%,2.5%and 3.5%in mass） or B2O3 （6%and 9%in mass） infused silica powders,respectively and then were fired at 1 150℃for 4 h,1 200℃for 4 h,and 1 350℃for 0.5 h,respectively.The bulk density,apparent porosity,cold modulus of rupture and thermal expansion coefficient of the fired specimens were determined,and phase compositions and microstructure were researched.The results show that:（1 ） B4C promotes the sintering of fused silica ceramics,but many closed pores will form easily with B4 C increase; （2） fused silica ceramics with 3.5 mass%B4C have 1.045×10-6 V-1 of the lowest average thermal expansion coefficient between 40℃and 730℃;（3 ） B4C additive is more effective to restrain crystallization of fused silica than B2O3 with the same content of boron.