Abstract:B4C ceramics were strengthened by introducing the hard second–phase particles TiB2 and SiC, and the effects of TiB2 and SiC contents on the microstructure and properties of the composites were investigated. B4C–TiB2 binary composites with TiB2 contents of 10, 20, 30, and 40 vol% were prepared by hot pressing. The microstructure, mechanical properties, and electrical properties of the composites with different TiB2 contents were investigated and compared. The results showed that the B4C–30 vol%TiB2 composite obtained the best comprehensive properties, with a relative density, hardness, bending strength, fracture toughness, and conductivity of 97.9 %, 29.5 GPa, 590 MPa, 6.41 MPa m1/2, and 7.6 × 104 S/m. The compressive stress generated on B4C, crack deflection induced by TiB2, and conductive network formed by TiB2 are of great significance in the context of the properties of the B4C–TiB2 composites. In addition, B4C–TiB2–SiC ternary composites with SiC contents of 0, 10, and 20 vol% were also fabricated by hot pressing. The effect of SiC content on the microstructure and mechanical properties, and the effect of SiC on the antioxidant properties of the composites were investigated. The results showed that the B4C–30 vol%TiB2–10 vol%SiC composite had the best comprehensive properties, with a relative density, hardness, flexural strength, fracture toughness, and residual flexural strength (1600 ℃) of 98.8 %, 29.5 GPa, 621 MPa, 6.80 MPa m1/2, and 465 MPa. The inhibition of the growth of SiC to other grains, removal of oxide impurities, and repair of damage by SiC oxidation products play an important role in the performance of the B4C–TiB2–SiC composites.

Studies of microstructure and mechanical properties of SiC/B4C composites based on reaction sintering

Microstructural Characteristics of Reaction-Bonded B4C/SiC Composite

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Microstructures and mechanical properties of B4C‐SiC and B4C‐SiC‐TiB2 ceramic composites fabricated by hot pressing

Microstructure and properties of hot pressed TiB2 and SiC reinforced B4C–based composites

Influence of Silicon Addition on the Sintering Behavior and Mechanical Properties of Boron Carbide by SPS Process

B4C-SiC skeleton reinforced graphite composites with excellent mechanical properties

The Effect of CNTs on the Spark Plasma Sintering Densification Behavior and Mechanical Properties of B4C-Si Powders

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

Microstructures and mechanical properties of in-situ SiC-TiB2 ceramic composites fabricated by reactive melt infiltration

PREPARATION OF SiC-B4C COMPOSITE FILM AND ITS MECHANICAL AND THERMOELECTRIC PROPERTIES

Processing and mechanical properties of B4C-SiCw ceramics densified by spark plasma sintering

Microstructure and mechanical behaviour of transient liquid phase spark plasma sintered B4C–SiC–TiB2 composites from a B4C–TiSi2 system

Microstructure and mechanical properties of spark plasma sintered SiC ceramics aided by B4C

Effects of SiC on the microstructures and mechanical properties of B4C–SiC–rGO composites prepared using spark plasma sintering

Effects of SiC contents on the microstructure and mechanical properties of Al4SiC4–SiC ceramic composites

High-performance B4C matrix composites fabricated from the B4C–Si–CeO2 system via reactive hot pressing

Microstructure and mechanical property of B4C–SiC–CrB2 composites fabricated via reactive hot pressing

Effect of B2O3 Addition on Low-temperature Sintering Behavior and Properties of SiC/h-BN Multiphase Ceramics

Microstructure, mechanical properties and thermal shock behavior of h-BN-SiC ceramic composites prepared by spark plasma sintering