Study on Process of Smelting Antimony Using Bismuth Refining Dust as Raw Material

ZHENG Ya-jie,HONG Bo,TENG Hao,YANG Xing-wen

DOI: https://doi.org/10.3969/j.issn.0253-6099.2010.06.017

2010-01-01

Abstract:Using arsenic-bearing bismuth refining dust as raw material,antimony was smelted by the process of hydrochloric acid leaching-hydrolysis-conversion-reduction smelting.The leaching rate of antimony can reach 99.5% by leaching bismuth refining dust with hydrochloric acid under the conditions that the ratio of solid to liquid was 1∶3,reaction time was 4 h,reaction temperature was 80 ℃ and the dosage of hydrochloric acid was 1.2 times of theoretical dosage.Antimony oxychloride was obtained under the conditions that the dilution ratio of hydrochloric acid leaching solution was 10∶1,hydrolysis temperature was 25 ℃ and hydrolysis time was 1 h.Antimony oxychloride was converted into antimony trioxide in which the purity was 90.76% under the conditions that the ratio of solid to liquid was 1∶1.6,reaction temperature was 25 ℃,reaction time was 1 h and the dosage of ammonia water was 1.2 times of theoretical dosage.The effects of temperature,reaction time,the dosage of reductant anthracite coal and the dosage of fluxing agent sodium carbonate on direct recovery ratio of antimony were investigated experimentally.The content of metal antimony prepared by reduction smelting was 99.04% and the direct recovery ratio of antimony reached 93.2% under the conditions that the reacction temperature was 1 100 ℃,reaction time was 45 min and the dosage of reductant anthracite coal and fluxing agent sodium acarbonate were equivalent to 4.9% and 4.32% of the mass of antimony trioxide respectively.