Abstract:The Ni-Al intermetallic sheets were prepared by the reaction synthesis of pure Ni and Al foils with different thickness ratios. The first stage was performed at 640 °C/20 MPa/6 h to consume Al layers, and the second stage was performed at 1200 °C/20 MPa/1 h to complete the synthesis of Ni-Al intermetallic sheets. The thickness ratios of original Ni and Al foils strongly affected the microstructure and mechanical properties of Ni-Al intermetallic sheets. When Ni/Al thickness ratio was 1:1.5 (R1:1.5), the microstructure was single-phase NiAl with bimodal grain structure, and it transformed into coarse grains dominated single-phase NiAl structure when Ni/Al thickness ratio was 1:1 (R1:1). The microstructures changed to NiAl+Ni3Al+Ni when the ratios were 1:0.63 (R1:0.63) and 1:0.25 (R1:0.25). At ambient temperature, Samples R1:0.25 and R1:0.63 had high strength, while Samples R1:1 and R1:1.5 showed serious brittleness. At high temperature, Sample R1:1 showed preferable ductility with the elongation of 61.3%, 71.4% and 101.3% at 800 °C, 900 °C and 1000 °C, respectively; Sample R1:0.63 showed the highest tensile strength, with the values of 350.3 MPa, 230.5 MPa and 140.2 MPa at 800 °C, 900 °C and 1000 °C, respectively. For the fracture at ambient temperature, Sample R1:0.25 showed a mixed fracture mode of dimple fracture and quasi-cleavage fracture; the fracture mode of Sample R1:0.63 was mainly cleavage fracture; Sample R1:1 showed a typical brittle cleavage fracture with a large number of river-like patterns; the fracture mode of Sample R1:1.5 was brittle transgranular fracture for coarse grain layers (CGLs) and intergranular fracture for fine grain layers (FGLs). At high temperature, Samples R1:1.5 and R1:1 were mixed fracture modes of dimple fracture and quasi-cleavage fracture; the fracture mode of Sample R1:0.63 was mixed quasi-cleavage and cleavage fracture; the fracture mode of Sample R1:0.25 was single cleavage fracture with microcracks at the NiAl layers.

Three stage yielding phenomenon in a NiAlFe alloy

The Mechanical Properties of Intermetallic Ni50−xTi50Alx Alloys (X=6,7,8,9)

Improving the ductility of high-strength multiphase NiAl alloys by introducing multiscale high-entropy phases and martensitic transformation

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

Microstructures and Mechanical Behaviors of NiAlFe Intermetallic Compounds

Microstructure and Mechanical Properties of Ni3Al and Ni3Al–1B Alloys Fabricated by SHS/HE

Study on High Temperature Mechanical Behavior and Microstructure Evolution of Ni3Al-based Superalloy JG4246A

Investigating the Influence of Al Contents on Microstructure and Mechanical Properties of Ni 3 Al Superalloy Fabricated by Twin Wire‐Based Direct Arc Energy Deposition

The microstructure and mechanical properties of reaction synthesized Ni-Al intermetallic sheets by pure Ni/Al foils with different thickness ratios

Anomalous Yield and Intermediate Temperature Brittleness Behaviors of Directionally Solidified Nickel-Based Superalloy

Effect of Fe Addition on Microstructure and Properties of Al-3ni Alloys

Microstructure Characteristics and Compressive Properties of NiAl-based Multiphase Alloy During Heat Treatments

Molecular Dynamics Simulation of Tensile Mechanical Properties of Ni/Ni<sub>3</sub>Al

High-temperature tensile properties and deformation behavior of a multi-phase FeNiCrAlTi alloy

Alloying Effect on the Microstructure and Property of Single Crystal Ni 3 Al Alloys

Revealing mechanical property–strengthening micro-mechanism of Ni/Ni3Al-based alloys by molecular dynamics simulation

The composite microstructures’ effect on the mechanical properties of Ni–25Al–xFe intermetallics

Microstructure and Elevated Temperature Tensile Behaviour of Directionally Solidified Nickel Based Superalloy

Microstructural evolution and mechanical properties of Ni/Al reactive nanolaminates with different NixAly intermetallic phases

Fabrication and mechanical properties of the NiAl sheet with a 3-dimensional network structure prepared by Ni nets and Al foils

Dependence of Mechanical Properties on the Site Occupancy of Ternary Alloying Elements in Γ'-Ni3al: Ab Initio Description for Shear and Tensile Deformation