Abstract:Aluminum foam that is lightweight with high specific strength, high energy absorption and other characteristics can be used in aerospace, transportation, machinery manufacturing and other fields. The PCM method is usually used to prepare closed-cell aluminum foams. The microsized aluminum foams made by this process can solve the non-uniform pore structures caused by liquid drainage during the foaming process of large aluminum foams. The surface morphology and internal pore structure of microsized aluminum foams are affected by the quality of the precursor used for foaming. In this paper, foamable precursors were obtained via either hot rolling or hot extrusion and subsequently foamed. By analyzing the micromorphology and foaming process of the precursor, the influence of the technological method on the macroscopic pore structure of the final aluminum foam was studied. The results show that the aluminum powder particles in the precursor prepared with the hot rolling method had metallurgical bonding, and the outer surface was dense, with almost no porosity and holes in the interior. The microsized aluminum foam obtained after foaming was smooth in appearance, and the internal pore structure was round and uniform. The reason is that during the foaming process of microsize aluminum foam, the foaming agent was evenly distributed in the precursor of the hot rolling process because of its compact structure. During the foaming process, the decomposed gas of the foaming agent will not escape, and the evenly distributed foaming agent tends to nucleate in situ. In the process of rapid foaming, the pressure in the bubble is enough to resist the liquid drainage phenomenon caused by gravity, and the growth direction of the gas core is isotropic, which promotes the foam structure to be more rounded and uniform.

Preparation Methods of Aluminum Foams and Aluminum Foam Sandwichs

Fabrication, Processing, Properties, and Applications of Closed-Cell Aluminum Foams: A Review

Preparation Technology of Aluminum Foam Sandwich Panels by Powder Metallurgy and Optimization of Cellular Structure

Aluminum Foam Sandwiches: A Lighter Future for Car Bodies

Fabrication, properties, and applications of open-cell aluminum foams: A review

Preparation of aluminum foam sandwich with metallurgical bonding using friction stir welding

Microstructure and Compressive Properties of Aluminum Foams Made by 6063 Aluminum Alloy and Pure Aluminum

Effects of Aluminum Foam Filling on Compressive Strength and Energy Absorption of Metallic Y-Shape Cored Sandwich Panel

Study on the Process of Preparing Aluminum Foam Sandwich Panel Precursor by Friction Stir Welding

Properties of Aluminum Foam Prepared by Gas Injection Method

A Novel Hot-Pressing Method to Prepare Foamable Precursor of Aluminum Foam Sandwich (AFS)

Foaming Behavior of Microsized Aluminum Foam Using Hot Rolling Precursor

Research on Key Technologies for Batch Preparation of Aluminum Foam Slabs by Melt Foaming Process

A Review of Different Manufacturing Methods of Metallic Foams

Mechanical properties and energy absorption capabilities of aluminium foam sandwich structure subjected to low-velocity impact

Microstructural characteristics and mechanical properties of 7075 aluminum alloy foam sandwich panels fabricated via integrated forming and foaming

Foaming Process and Properties of 6063 Aluminum Foams by Melt Foaming Method

Preparation and Compressive Performance of an A356 Matrix Syntactic Foam

Preparation of Shaped Aluminum Foam Parts by Investment Casting

Preparation of Aluminum Foam by Gas Injection Foaming

Dynamic response and energy absorption of aluminum foam sandwich under low-velocity impact