Regulating the interfacial reaction between carbon nanotubes and aluminum via copper nano decoration
Baisong Guo,Siwei Luo,Yue Wu,Min Song,Biao Chen,Zhentao Yu,Wei Li
DOI: https://doi.org/10.1016/j.msea.2021.141576
2021-07-01
Abstract:<p>The interfacial reaction plays a decisive role in the mechanical performances of the aluminum matrix composites reinforced with nano carbonaceous materials such as carbon nanotubes (CNTs). Due to the low Gibbs energy of Al<sub>4</sub>C<sub>3</sub> formation and the required high-temperature processes for fabricating densified Al/CNTs composites, it is difficult to regulate the extent of the chemical reaction between Al matrix and CNTs, the dispersed CNTs are easily consumed to be Al<sub>4</sub>C<sub>3</sub> rods. In this work, the Cu nano decoration on the surface of CNTs was proposed to restrict the massive formation of Al<sub>4</sub>C<sub>3</sub>. Raman results and systematical observations of transmission electron microscopy (TEM) revealed that the quantity and size of Al<sub>4</sub>C<sub>3</sub> highly relate to the annealing time, and the pre-coating of Cu on the surface of CNTs can effectively limit the Al<sub>4</sub>C<sub>3</sub> formation during the annealing process. Moreover, for the composite reinforced with Cu-coated CNTs, the microhardness, Young's modulus, and tensile properties can be optimized by controlling the annealing time. When the composite reinforced with Cu-coated CNTs was annealed at 550 °C for 12 h, the highest ultimate tensile strength (418 ± 6.5 MPa) together with good ductility (10.7 ± 0.3%) can be achieved, which can be mostly attributed to the limit formation of Al<sub>4</sub>C<sub>3</sub>. This work provides an effective approach to regulate the interfacial reaction in Al/CNTs composite and achieve higher mechanical performance accordingly.</p>
materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering