Abstract:The structure, phase composition, hardness, and tribological properties of composite gas-thermal 50% Cu–50% (Al–Si) coatings under various friction conditions were studied. It has been shown that during the process of high-speed metallization, active interaction of molten aluminum and copper particles occurs, leading to the formation of solid solutions and intermetallic compounds in sprayed coatings. In particular, in 50% Cu–50% (Al–Si) coatings, in addition to the matrix phases of Cu and Al, intermetallic compounds Cu 9 Al 4 , CuAl 2 , and Cu 3 Al are recorded. The hardness and microhardness of the composite are 180 HV 1 and 180–190 HV 0.025, respectively. It has been established that a composite coating of 50% Cu–50% (Al–Si) has higher wear resistance under various friction conditions than the widely used coating of CuSn11P-C antifriction bronze, obtained by centrifugal induction surfacing. In particular, in the environment of I-20A lubricant, the wear resistance of the composite coating exceeds the wear resistance of bronze by ≈1.2 times, in the environment of Litol-24 plastic lubricant, by ≈1.4 times, and with dry friction up to ≈2.8 times. It has been shown that during boundary friction, dislocations accumulate in aluminum particles of the composite, while in copper particles at elevated test pressures, a predominant formation of a subgrain structure occurs. Based on the studies conducted, it was concluded that the increased wear resistance of the composite is due to the presence of solid intermetallic compounds in it, solid solution strengthening, the presence of silicon in aluminum interlayers, as well as dislocation strengthening of aluminum interlayers and the formation of a subgrain structure in copper interlayers.

Friction and wear behavior of CuFe3Al powder metallurgical composites in dry sliding

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Mechanical and tribological property of Cu/CrB 2 composites under dry sliding condition

Tribological behavior of aluminum matrix composites reinforced with ceramic particulates in dry sliding against a semimetallic friction material

Dry sliding wear behavior of in situ Cu–TiB2 nanocomposites against medium carbon steel

Torsional Fretting and Torsional Sliding Wear Behaviors of CuNiAl Against 42crmo4 under Dry Condition

Dry Sliding Friction and Wear Behavior of CuZn39Pb2 and AA7075 Under Industrial and Laboratory Conditions

Tribological Behavior and Wear Mechanism of Cu-SiO2 Sintered Composite under Different Sliding Speeds

Influence of Cu content on mechanical and tribological properties of Al–7Si–Cu alloy

Study of Friction and Wear Properties of Cu/Short Carbon Fibers Composites

Influence of re-melting rate on the dry sliding wear characteristics of LPBFed Cu–Cr–Zr alloy

Friction and Wear Behavior of Copper-Graphite Composite Material in High-Speed Sliding with Current

Dry sliding friction and wear properties of B4C particulate-reinforced Al-5083 matrix composites

Study on the Tribological Performance of Copper-Based Powder Metallurgical Friction Materials with Cu-Coated or Uncoated Graphite Particles as Lubricants

Study on friction and wear behavior of copper fibers in semimetallic friction materials

Dry sliding tribological properties of Cu-WS 2 self-lubricating composites at 25–500 °C

Effect of Cr–Fe on friction and wear properties of Cu-based friction material

Carbon Fiber Reinforced Carbon–Al–Cu Composite for Friction Material

Substructural Changes in the Surface Layers of Composite Gas-Thermal Cu–(Al–Si) Coatings during Friction under Various Conditions

Tribology performance of Cu-C/C composites with and without current

Wear and Frictional Behavior of Copper Modified Ti-6Al-4V Alloy