Abstract:To clarify the effect of aging treatment on the microstructure and properties of Cu–3Ti–2Mg alloy, a Cu–3Ti–2Mg alloy ingot was fabricated, followed by homogenizing at 800 °C for 10 h, solubilizing at 750 °C for 4 h and aging at different temperatures. The microstructure was characterized by SEM, EPMA, TEM, 3D laser scanning microscope and Raman spectroscope, and the mechanical properties, electrical conductivity and tribological performance of Cu–3Ti–2Mg alloy was tested. The results showed that the diffraction peaks of Cu gradually shift to the left with increase of the aging temperature, indicating Ti precipitate from the Cu matrix. The interfaces between precipitation phases and Cu matrix exhibit a clean and tight bond without visible defects. With increase of aging temperatures, more Ti precipitated from Cu matrix enhances the electrical conductivity, hardness and elasticity modulus are increased due to the formation of β′-Cu4Ti, β-Cu3Ti and Cu2Mg phase. Friction test indicated that the precipitation strengthening improves the wear resistance of the Cu–3Ti–2Mg alloy and the alloy after aging at 500 °C has the lowest wear rate of 2 × 10−5 g/Nm. The Raman analysis revealed that the tribofilm formed on the wear surface is consisted of Cu2O. Based on the analysis for the mechanical properties and tribological behaviors analysis as the function of the aging temperature of the Cu–3Ti–2Mg alloy, it suggests that the synergistic effect between β′-Cu4Ti phase and Cu2Mg phase endows the possibility for the alloy to be used under the conductive friction service condition.

Wear and Frictional Behavior of Copper Modified Ti-6Al-4V Alloy

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

The Relationships Between Tribological Behaviour and Heat-Transfer Capability of Ti6Al4V Alloys

Correlation between the characteristics of the thermo-mechanical mixed layer and wear behaviour of Ti–6Al–4V alloy

Dry Friction Characteristics of Ti-6Al-4V Alloy under High Sliding Velocity

Tribology properties of additively manufactured Ti6Al4V alloy after heat treatment

Study on improved tribological properties by alloying copper to CP-Ti and Ti–6Al–4V alloy

Time-frequency analysis of the tribological behaviors of Ti6Al4V alloy under a dry sliding condition

Solutionizing Temperature Effect on the Dry Sliding Wear Performance of Al-7Si-0.3Mg-3Ni Hypoeutectic Alloy

Microstructure evolution, mechanical properties and tribological behaviors of copper alloy aged at different temperatures

Effect of high temperatures on dry sliding friction and wear behaviour of CuCrZr copper alloy

Friction and wear of titanium alloys sliding against metal, polymer, and ceramic counterfaces

The Effect of Copper Content on the Mechanical and Tribological Properties of Hypo-, Hyper- and Eutectoid Ti-Cu Alloys

Microstructure and mechanical properties of Cu-12 Al-6 Ni with Ti addition prepared by powder metallurgy

Dry sliding wear behavior of in situ Cu–TiB2 nanocomposites against medium carbon steel

MORPHOLOGY OF WEAR DEBRIS DURING DRY SLIDING OF Ti6Al4V/TiC COMPOSITE AT ELEVATED TEMPERATURES IN VACUUM CONDITIONS

Microstructural changes and dry sliding wear behavior of Cu-15Ni-8Sn-0.5Co alloy during deformation and aging treatment

Tribological Properties of Additive Manufactured Ti6Al4V Against Cemented Carbide under Dry Sliding Conditions

Thermal effects on wear behavior of additively manufactured NiTi shape memory alloys

Sliding Wear Behavior of Fully Nanotwinned Cu Alloys

Wear performance of Ti-6Al-4 V titanium alloy through nano-doped lubricants