Abstract:Core-shell structured SiC/SiO2 nanowires (SiC/SiO2 NWs) were synthesized by a simple thermal evaporation method without a catalyst. The influence of the growth temperature and holding time on the microstructure and composition of the nanowires were investigated. The results indicate that within the temperature range of 1150 to 1550 degrees C, the color of SiC/SiO2 nanowires gradually transitions from pure white to off-white with increasing temperature. During this process, the average diameter of SiC/SiO2 increases from 74 nm to 291 nm, while the surface SiO2 layer thickness decreases from 17 nm to 5 nm, with nanowires can reach lengths of hundreds of micrometres. Variations in supersaturation of SiO and CO at different temperatures lead to discrepancies in nanowire diameter and SiO2 shell thickness. At 1350 degrees C, prolonged holding time enhances silicon powder reaction, resulting in increased structural disorder of the obtained SiC/SiO2 nanowires. The nanowire growth follows a vapor-solid (V-S) mechanism. Additionally, the study demonstrates that the photoluminescence (PL) characteristics of the nanowires exhibit a blue shift attributable to their nanoscale dimensions, while variations in emission spectra correlate with stacking faults, SiC diameter, and SiO2 thickness. This work may be provide a theoretical basis for preparing SiC/SiO2 nanowires with different diameters and SiO2 shell thicknesses, which is crucial for advancing the development and application of SiC/SiO2 nanoceramics.

Synthesis and Photoluminescence of Amorphous SiO2 Nanowires

Ultrafast growth of single-crystalline Si nanowires

Synthesis and Photoluminescence Properties of Amorphous Siox Nanowires

Amorphous SiO2 Nanoparticles Grown on the Surface of the Nanowires

Amorphous SiO<inf>2</inf> nanoparticles grown on the surface of the nanowires

Synthesis and Photoluminescence of Ultralong Amorphous SiO2 Nanowires Catalysed by Germanium

Tiny SiO2 nano-wires synthesized on Si (111) wafer

Selective Synthesis of Sio2 Nws on Si Substrate and Their Adjustable Photoluminescence

Parallel Ultrafine SiO2 Nanowires Coated with Amorphous SiO2

SiO2 Nano-Crystals Embedded in Amorphous Silica Nanowires

Synthesis and Characterization of Ultra-Long Silica Nanowires

Synthesis and Raman Spectra of Si-Nanowires

Tiny SiO2 nano-wires synthesized on Si (1 1 1 ) wafer

Synthesis and Characterization of Amorphous SiOx Nanowires Prepared by Vapor Phase Transport Process

Synthesis and Characterization of Amorphous SiO2 Nanowires Via Pulsed Laser Deposition Accompanied by N2 Annealing

Synthesis and photoluminescence properties of single crystal ZnO nanowires by thermal evaporation

Synthesis and light emission of fine and straight Si nanowires

Preparation and Characterization of Amorphous Siox Nanowires

Synthesis of Α–sio 2 Nanowires Using Au Nanoparticle Catalysts on a Silicon Substrate

Si Nanocrystals Embedded in SiO 2 Nano-Networks

In-situ Synthesis of SiC/SiO2 Nanowires by Catalyst-Free Thermal Evaporation of Silicon Powder and Their Photoluminescence Properties