Abstract:Mechanochemically synthesized MoSi2‐ and WSi2‐reinforced Al–Cu alloys are synthesized using mechanical alloying and pressureless sintering. Addition of MoSi2 and WSi2 particulates improves the mechanical properties of alloys. The highest hardness (≈165 HV) and the lowest wear volume loss (≈0.17 mm3) are obtained from the 5 wt% WSi2‐reinforced composite. Herein, investigations on the microstructural, physical, and mechanical properties of molybdenum disilicide (MoSi2)‐ and tungsten disilicide (WSi2)‐reinforced aluminum (Al)–copper (Cu) matrix composites are reported. Powder metallurgy methods such as mechanochemical synthesis (MCS), mechanical alloying (MA), cold pressing, and pressureless sintering are combined to produce composites. First of all, MoSi2 and WSi2 nanoparticles are synthesized by MCS and selective acid leaching, yielding reinforcement materials for Al–Cu matrix. Powder blends consisting of 95 wt% Al and 5 wt% Cu are mixed with metal disilicides at different weight percentages (1, 2, and 5 wt%). MA for 4 h is conducted on these overall blends using a high‐energy ball mill. Microstructural and thermal properties of the as‐blended and mechanically alloyed powders are determined, and then they are compacted under 450 MPa and sintered at 550 °C for 2 h. Mechanical characterization of the composites reveals an increase in hardness and wear resistance with an increasing amount of reinforcement content. Among bulk samples, 5 wt% WSi2‐reinforced composites have the highest microhardness (165 ± 15 HV) and lowest wear rate (1.69 × 106 μm3 Nm−1) values. However, under the compression forces, the highest toughness and strength are obtained from 2 wt%‐reinforced composites.

Synthesis and properties of MoSi2 alloyed with aluminum

Synthesis of Mo(Si, Al)2 Powders by Mechanical Alloying

Effect of silicon addition on microstructure and mechanical properties of a high strength Ti-4Al-4Mo-4Sn alloy prepared by powder metallurgy

Microstructure and compression properties of fine Al2O3 particles dispersion strengthened molybdenum alloy

Synthesis and properties of MoAlB composites reinforced with SiC particles

The Effect of Si Content on the Microstructure and Mechanical Properties of Al–1.2Mg–xSi–1.2Cu–0.6Mn Cast Alloy

Effects of metalloid Si on the microstructure and mechanical properties of Fe36Ni36Cr10Mo1Al17-XSiX alloys

Synthesis of a novel MoSS+Mo5SiB2+Mo5Si3 based Mo–Si–B alloy and its enhanced fracture toughness

Developing a uniform distribution of bimodal α-Mo grains in the Mo–Si–B alloy for toughness and strength improvement

Preparation, microstructure and mechanical properties of MoAlB-0.15% Si ceramics with superior strength and toughness

Effect of Si on Fe-rich intermetallic formation and mechanical properties of heattreated Al-Cu-Mn-Fe alloys

Synergistic effect of Zr and Mo on precipitation and high-temperature properties of Al-Si-Cu-Mg alloys

Mechanical Performances of Al-Si-Mg Alloy with Dilute Sc and Sr Elements

Tailoring the strengthening-toughening behavior of the MoSi2 film by doping trace solute Au

Microstructure and mechanical properties of a Mo-toughened Mo 3 Si-based in situ nanocomposite

Microstructure and mechanical properties of Si micro-alloyed (Ti28Zr40Al20Nb12)100-xSix (x=0, 0.1, 0.2, 0.5) high entropy alloys

Microstructure, mechanical properties and tribocorrosion characteristics of (Mo1-xCrx)5Si3 alloys

Powder Metallurgical Processing of Al–5 wt% Cu Matrix Composites Reinforced with MoSi2 and WSi2 Particulates

Microstructure evolution and mechanical properties of selective laser melting fabricated hybrid particle reinforced AlSi10Mg composites

Optimizing the microstructure and mechanical behaviors of bimodal Mo-Si-B alloy by heat treatment

Effect of Si on Phase Equilibria, Mechanical Properties and Tribological Behaviour of Al-Cu Alloy